Overview of materials for Polypropylene with 10% Glass Fiber Filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene with 10% Glass Fiber Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Glass Fiber Filler". Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.930 - 1.45 g/cc
0.0336 - 0.0524 lb/in³
Average value: 1.01 g/cc Grade Count:110
Filler Content 5.00 - 13.0 %
5.00 - 13.0 %
Average value: 10.1 % Grade Count:55
Water Absorption 0.0100 - 0.150 %
0.0100 - 0.150 %
Average value: 0.0190 % Grade Count:20
Additive Loading 10.0 %
10.0 %
Average value: 10.0 % Grade Count:4
Linear Mold Shrinkage 0.00100 - 0.0390 cm/cm
0.00100 - 0.0390 in/in
Average value: 0.00750 cm/cm Grade Count:94
Linear Mold Shrinkage, Transverse 0.00620 - 0.0210 cm/cm
0.00620 - 0.0210 in/in
Average value: 0.0156 cm/cm Grade Count:8
Melt Flow 1.00 - 15.0 g/10 min
1.00 - 15.0 g/10 min
Average value: 8.72 g/10 min Grade Count:73
Ash 10.0 - 29.0 %
10.0 - 29.0 %
Average value: 12.8 % Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Rockwell R 76.0 - 110
76.0 - 110
Average value: 90.4 Grade Count:28
Hardness, Shore D 32.0 - 73.0
32.0 - 73.0
Average value: 69.3 Grade Count:23
Tensile Strength, Ultimate 20.0 - 55.8 MPa
2900 - 8100 psi
Average value: 42.6 MPa Grade Count:74
Tensile Strength, Yield 21.0 - 75.0 MPa
3050 - 10900 psi
Average value: 43.2 MPa Grade Count:39
Elongation at Break 1.50 - 34.0 %
1.50 - 34.0 %
Average value: 7.31 % Grade Count:69
Elongation at Yield 2.00 - 10.0 %
2.00 - 10.0 %
Average value: 4.56 % Grade Count:21
Modulus of Elasticity 1.70 - 5.17 GPa
247 - 750 ksi
Average value: 2.95 GPa Grade Count:46
Flexural Yield Strength 29.0 - 90.0 MPa
4200 - 13100 psi
Average value: 57.7 MPa Grade Count:74
Flexural Modulus 1.20 - 4.30 GPa
174 - 624 ksi
Average value: 2.43 GPa Grade Count:106
Compressive Yield Strength 47.6 - 52.4 MPa
6900 - 7600 psi
Average value: 49.1 MPa Grade Count:4
Izod Impact, Notched 0.267 - 3.74 J/cm
0.500 - 7.00 ft-lb/in
Average value: 0.740 J/cm Grade Count:95
Izod Impact, Unnotched 1.33 - 5340 J/cm
2.50 - 10000 ft-lb/in
Average value: 4.39 J/cm Grade Count:41
Izod Impact, Notched (ISO) 5.00 - 20.0 kJ/m²
2.38 - 9.52 ft-lb/in²
Average value: 9.75 kJ/m² Grade Count:4
10.0 - 10.0 kJ/m²

@Temperature -30.0 - -30.0 °C
4.76 - 4.76 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 10.0 kJ/m² Grade Count:1
Charpy Impact Unnotched 2.00 - 5.00 J/cm²
9.52 - 23.8 ft-lb/in²
Average value: 3.80 J/cm² Grade Count:8
2.00 - 3.00 J/cm²

@Temperature -20.0 - -20.0 °C
9.52 - 14.3 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 2.45 J/cm² Grade Count:8
Charpy Impact, Notched 0.250 - 1.50 J/cm²
1.19 - 7.14 ft-lb/in²
Average value: 0.882 J/cm² Grade Count:11
0.100 - 0.700 J/cm²

@Temperature -20.0 - -20.0 °C
0.476 - 3.33 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 0.303 J/cm² Grade Count:11
Gardner Impact 0.339 - 4.51 J
0.250 - 3.33 ft-lb
Average value: 1.02 J Grade Count:29
1.90 - 1.90 J

@Temperature -20.0 - -20.0 °C
1.40 - 1.40 ft-lb

@Temperature -4.00 - -4.00 °F
Average value: 1.90 J Grade Count:1
Thermal Properties Metric English Comments
CTE, linear 37.8 - 68.4 µm/m-°C
21.0 - 38.0 µin/in-°F
Average value: 55.0 µm/m-°C Grade Count:13
Thermal Conductivity 0.159 - 0.187 W/m-K
1.10 - 1.30 BTU-in/hr-ft²-°F
Average value: 0.180 W/m-K Grade Count:4
Melting Point 136 - 170 °C
277 - 338 °F
Average value: 160 °C Grade Count:13
Deflection Temperature at 0.46 MPa (66 psi) 65.0 - 202 °C
149 - 396 °F
Average value: 142 °C Grade Count:80
Deflection Temperature at 1.8 MPa (264 psi) 46.0 - 155 °C
115 - 311 °F
Average value: 117 °C Grade Count:92
Vicat Softening Point 110 - 156 °C
230 - 313 °F
Average value: 138 °C Grade Count:11
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:41
Glow Wire Test 650 - 850 °C
1200 - 1560 °F
Average value: 717 °C Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+17 ohm-cm
1000 - 1.00e+17 ohm-cm
Average value: 8.62e+15 ohm-cm Grade Count:26
Surface Resistance 1e+05 - 1.00e+15 ohm
1e+05 - 1.00e+15 ohm
Average value: 2.22e+14 ohm Grade Count:9
Static Decay 1.00 - 2.00 sec
1.00 - 2.00 sec
Average value: 1.86 sec Grade Count:7
Dielectric Constant 2.50 - 2.90
2.50 - 2.90
Average value: 2.67 Grade Count:6
Dielectric Strength 19.3 - 22.4 kV/mm
490 - 570 kV/in
Average value: 21.1 kV/mm Grade Count:10
Dissipation Factor 0.00100
0.00100
Average value: 0.00100 Grade Count:6
Arc Resistance 80.0 - 132 sec
80.0 - 132 sec
Average value: 118 sec Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 166 - 240 °C
330 - 464 °F
Average value: 209 °C Grade Count:16
Nozzle Temperature 210 - 260 °C
410 - 500 °F
Average value: 218 °C Grade Count:24
Melt Temperature 180 - 260 °C
356 - 500 °F
Average value: 215 °C Grade Count:49
Mold Temperature 20.0 - 80.0 °C
68.0 - 176 °F
Average value: 45.0 °C Grade Count:65
Drying Temperature 65.6 - 82.2 °C
150 - 180 °F
Average value: 76.0 °C Grade Count:43
Moisture Content 0.0500 - 0.200 %
0.0500 - 0.200 %
Average value: 0.0568 % Grade Count:22
Injection Pressure 2.76 - 120 MPa
400 - 17400 psi
Average value: 56.9 MPa Grade Count:58