Polymer Property : Tensile Strength, Yield = 21.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Braskem LH 437 LMDPE Cast Film Extrusion Polyethylene  (discontinued **)
Applications: Diapers (back sheet); Absorbent pads (back sheet). Information provided by Braskem
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
LyondellBasell Pro-fax 8523 Polypropylene Impact Copolymer
Key Features: excellent cold impact resistance, good stiffness and impact balance, FDA acceptableApplications: automotive parts, luggage, totes, bins, carrying cases, appliancesMeets FDA requirement..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
LyondellBasell SEQUEL® E3000 TPO
Description: SEQUEL® E3000 thermoplastic olefinic elastomer (TPO) is designed for thermoformed exterior and interior applications that require toughness and dimensional stability. This extrusion..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Flint Hills AP6835-HS Polypropylene Impact Copolymer
Features: Excellent processing, good low temperature impact strength.Applications: Injection molding: Appliance components, consumer durables and closuresInformation Provided by Flint Hills Resource..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Ineos Styrenics 495F High-Impact Polystyrene Resin (Global)
Description: High-impact, high-flow grade for a wide variety of applications, including appliance components, consumer electronics housings, magnetic and optical media, building and construction, pa..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
IRPC Polimaxx Polene 2500TC Polypropylene Block Copolymer
CHARACTERISTICS: MEDIUM FLOW, HIGH IMPACTAPPLICATIONS: INJECTION MOLDING FOR ELECTRICAL APPLIANCES, AUTOPARTS, ICE CREAM CUPS, CONTAINERS
Tensile Strength, Yield >= 21.0 MPa
>= 3050 psi
Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite
Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended to be processed into pressure p..
Tensile Strength, Yield 21.0 MPa
3050 psi
ISO Method R527
LyondellBasell Astryn BR33GC Polypropylene Copolymer, Mineral Filled
Key Features: conventional melt flow, high modulus, UV-stabilized, mineral-filled polypropylene copolymer, high rigidity, high impact strength, good dimensional stability, low foggingApplications: k..
Tensile Strength, Yield 21.0 MPa
3040 psi
Spartech E65390 General Purpose PVC
First choice for compounds meeting the stringent requirements of Spiral Hose, Automotive, Housewares, Farm Equipment, Coated Fencing and numerous other applications including Lawn & Garden Wheels. B..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON MD000 PP
LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added feature of this material is: Electrically Conductive.
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene
DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. ..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
A. Schulman POLYFORT™ PP 7001
Information provided by A. Schulman.
Tensile Strength, Yield 21.0 MPa
3050 psi
50 mm/min, type I bar; ASTM D638
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors
DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene
DescriptionPolypropylene PP 1467-01ApplicationPP 1467-01 meet FDA Regulation 21 CFR 177.1520, for all food contact applications.Information provided by A. Schulman.
Tensile Strength, Yield >= 21.0 MPa
>= 3050 psi
Requirement
Westlake Plastics Lennite® GUR1020 (Type I) Ultra-high Molecular Weight Polyethylene For Medical Applications
Medical grade Lennite UHMWPE is produced from premium resins in accordance with ASTM specification F648 and International Standard ISO 5834-1 for surgical implants. Westlake Plastics' proprietary m..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Goodfellow TPX® MX002O Polymethylpentene
This grade is highly recommended for injection molding, film and mandrel extrusion; also for fiber extrusion and blow molding.TPX® is semi-crystalline, transparent, very light and - for a polyolefi..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
DescriptionPolyfort® FPP 3711 is a 26% calcium carbonate filled high impact polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield 21.0 MPa
3050 psi
ISO 527
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer
DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black
DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.
Tensile Strength, Yield 21.0 MPa
3050 psi
ISO 527-2
ExxonMobil Exxtral™ BMU 143 Performance Polyolefin
Product Description: A specialty thermoplastic polyolefin resin characterized by a good stiffness/toughness balance and designed for automotive interior application in which good surface finish, hig..
Tensile Strength, Yield 21.0 MPa
3050 psi
ISO 527-2
ExxonMobil Exxtral™ BMU 143S Performance Polyolefin
Product Description: A specialty thermoplastic polyolefin resin characterized by a good stiffness/toughness balance and designed for automotive interior application in which good surface finish, hig..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced
Tensile Strength, Yield 21.0 MPa

@Strain 0.200 %,
Temperature 1600 °C
3050 psi

@Strain 0.200 %,
Temperature 2910 °F
AK Steel 18 SR® Ferritic Stainless steel
AK Steel 18 SR® provides excellent resistance to high temperature scaling - far superior to that of Type 446 stainless steel. This material is readily welded by conventional methods. It is not su..
Tensile Strength, Yield 21.0 MPa
3050 psi
BASF Novolen® 3340 PC Polypropylene
Nucleated grade for injection moldings with higher transparency.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Yield 21.0 MPa
3050 psi
ISO R 527
Addiplast Addilene PMD 50284 Polypropylene Copolymer
Mineral reinforced, improved rigidityInformation provided by Addiplast.
Tensile Strength, Yield 21.0 MPa
3050 psi
Z direction; ASTM D638
ALM FR 106 Nylon 11 SLS Prototyping Polymer
This flame retardant rapid prototyping material has additives in the raw material that allows it to pass aeronautic standard FAR25.853 smoke, flame, and toxicity tests. This material is ideal for Ae..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Ineos Nova 5420 High Impact Polystyrene  (discontinued **)
High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheetProperties were determined on injection m..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Ineos Nova 5500 High Impact Polystyrene  (discontinued **)
Good overall balance of properties, USP Class VIApplications: Audio cassettes and cartridges, Housewares, Toys, Structural foam, Machine housings, Window framesProperties were determined on injectio..
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON MD000ISC PP
LNP STAT-KON* MD000ISC is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Tensile Strength, Yield 21.0 - 75.0 MPa
3050 - 10900 psi
Average value: 43.2 MPa Grade Count:39
Overview of materials for Polypropylene with 10% Glass Fiber Filler