Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00624 cm/cm Grade Count:194 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00550 cm/cm | 0.00100 - 0.00550 in/in | Average value: 0.00266 cm/cm Grade Count:23 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00327 cm/cm Grade Count:11 |
Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00429 cm/cm Grade Count:38 |
Overview of materials for Polystyrene + Polyphenylene Ether, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Unreinforced". Each property range of values reported is minimum and .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00443 cm/cm Grade Count:20 |
Overview of materials for Polyphenylene Ether, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 10% Glass Filled". Specific grades with glass content between 5% and 14% are includ.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00505 cm/cm Grade Count:5 |
Overview of materials for Polyphenylene Ether, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Mineral Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0220 cm/cm | 0.00100 - 0.0220 in/in | Average value: 0.00589 cm/cm Grade Count:58 |
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00514 cm/cm Grade Count:131 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded". Each property range of values reported is .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00900 cm/cm | 0.00100 - 0.00900 in/in | Average value: 0.00321 cm/cm Grade Count:56 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00900 cm/cm | 0.00100 - 0.00900 in/in | Average value: 0.00256 cm/cm Grade Count:72 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0300 cm/cm | 0.00100 - 0.0300 in/in | Average value: 0.00641 cm/cm Grade Count:75 |
Overview of materials for Polycarbonate, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Impact Modified". Each property range of values reported is minimum and maximum values of.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00443 cm/cm Grade Count:7 |
Overview of materials for Polycarbonate, Foam Grade, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Foam Grade, Glass Filled". Each property range of values reported is minimum and maximum .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0120 cm/cm | 0.00100 - 0.0120 in/in | Average value: 0.00503 cm/cm Grade Count:19 |
Overview of materials for Polycarbonate, Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Conductive". Each property range of values reported is minimum and maximum values of appr.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0180 cm/cm | 0.00100 - 0.0180 in/in | Average value: 0.00669 cm/cm Grade Count:113 |
Overview of materials for Polycarbonate/PET Polyester Blend This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend". Each property range of values reported is minimum and maximum values.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00514 cm/cm Grade Count:11 |
Overview of materials for Polycarbonate/PET Polyester Blend, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend, Glass Reinforced". Each property range of values reported is minimum .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00214 cm/cm Grade Count:13 |
Overview of materials for Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler". Specific grades with glass content between 45%.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0180 cm/cm | 0.00100 - 0.0180 in/in | Average value: 0.00226 cm/cm Grade Count:36 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00995 cm/cm Grade Count:40 |
Overview of materials for Nylon 66, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are inclu.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0300 cm/cm | 0.00100 - 0.0300 in/in | Average value: 0.00469 cm/cm Grade Count:144 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00500 cm/cm | 0.00100 - 0.00500 in/in | Average value: 0.00288 cm/cm Grade Count:3 |
Overview of materials for Nylon 11 with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are includ.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0120 cm/cm | 0.00100 - 0.0120 in/in | Average value: 0.00366 cm/cm Grade Count:16 |
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00290 cm/cm Grade Count:26 |
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00550 cm/cm | 0.00100 - 0.00550 in/in | Average value: 0.00139 cm/cm Grade Count:21 |
Overview of materials for Nylon 12, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0350 cm/cm | 0.00100 - 0.0350 in/in | Average value: 0.00738 cm/cm Grade Count:232 |
Overview of materials for Nylon 6, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Heat Stabilized". Each property range of values reported is minimum and maximum values of appro.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0150 cm/cm | 0.00100 - 0.0150 in/in | Average value: 0.00465 cm/cm Grade Count:33 |
Overview of materials for Nylon 66, Glass Fiber/MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/MoS2 Filled". Each property range of values reported is minimum and maximum values.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0500 cm/cm | 0.00100 - 0.0500 in/in | Average value: 0.00570 cm/cm Grade Count:30 |
Overview of materials for PVC, Molded This property data is a summary of similar materials in the MatWeb database for the category "PVC, Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00253 cm/cm Grade Count:16 |
Overview of materials for Polyphenylene Ether, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 30% Glass Filled". Specific grades with glass content between 25% and 34% are inclu.. |
|||
Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00511 cm/cm Grade Count:287 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |