Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.23 - 1.47 g/cc
0.0444 - 0.0531 lb/in³
Average value: 1.37 g/cc Grade Count:53
Filler Content 30.0 - 33.0 %
30.0 - 33.0 %
Average value: 30.9 % Grade Count:10
Water Absorption 0.500 - 7.00 %
0.500 - 7.00 %
Average value: 3.70 % Grade Count:33
Moisture Absorption at Equilibrium 1.00 - 2.50 %
1.00 - 2.50 %
Average value: 1.89 % Grade Count:27
Water Absorption at Saturation 3.50 - 6.50 %
3.50 - 6.50 %
Average value: 5.20 % Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.0200 cm/cm
0.00100 - 0.0200 in/in
Average value: 0.00367 cm/cm Grade Count:47
Linear Mold Shrinkage, Transverse 0.00500 - 0.0130 cm/cm
0.00500 - 0.0130 in/in
Average value: 0.00821 cm/cm Grade Count:37
Melt Flow 2.00 - 45.0 g/10 min
2.00 - 45.0 g/10 min
Average value: 17.3 g/10 min Grade Count:3
Mechanical Properties Metric English Comments
Ball Indentation Hardness 80.0 - 270 MPa
11600 - 39200 psi
Average value: 180 MPa Grade Count:22
Tensile Strength, Ultimate 2.20 - 361 MPa
319 - 52400 psi
Average value: 143 MPa Grade Count:46
28.5 - 114 MPa

@Temperature 150 - 220 °C
4130 - 16500 psi

@Temperature 302 - 428 °F
Average value: 61.8 MPa Grade Count:1
Tensile Strength, Yield 70.0 - 184 MPa
10200 - 26700 psi
Average value: 121 MPa Grade Count:13
Elongation at Break 2.00 - 35.0 %
2.00 - 35.0 %
Average value: 5.00 % Grade Count:47
2.50 - 3.00 %

@Temperature 210 - 230 °C
2.50 - 3.00 %

@Temperature 410 - 446 °F
Average value: 2.75 % Grade Count:1
2.50 - 3.00 %

@Time 1.80e+6 - 1.80e+7 sec
2.50 - 3.00 %

@Time 500 - 5000 hour
Average value: 2.75 % Grade Count:1
Elongation at Yield 4.00 - 6.00 %
4.00 - 6.00 %
Average value: 4.56 % Grade Count:7
Modulus of Elasticity 1.80 - 11.0 GPa
261 - 1600 ksi
Average value: 7.95 GPa Grade Count:43
Flexural Yield Strength 56.0 - 275 MPa
8120 - 39900 psi
Average value: 205 MPa Grade Count:24
Flexural Modulus 3.70 - 9.50 GPa
537 - 1380 ksi
Average value: 7.89 GPa Grade Count:23
Poissons Ratio 0.370 - 0.400
0.370 - 0.400
Average value: 0.390 Grade Count:3
Izod Impact, Notched 0.550 - 1.50 J/cm
1.03 - 2.81 ft-lb/in
Average value: 1.04 J/cm Grade Count:4
Izod Impact, Notched (ISO) 6.20 - 22.0 kJ/m²
2.95 - 10.5 ft-lb/in²
Average value: 12.0 kJ/m² Grade Count:12
12.0 - 19.0 kJ/m²

@Temperature -30.0 - -30.0 °C
5.71 - 9.04 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 15.5 kJ/m² Grade Count:2
Charpy Impact Unnotched 2.50 J/cm² - NB
11.9 ft-lb/in² - NB
Average value: 6.80 J/cm² Grade Count:41
2.40 J/cm² - NB

@Temperature -40.0 - 30.0 °C
11.4 ft-lb/in² - NB

@Temperature -40.0 - 86.0 °F
Average value: 5.44 J/cm² Grade Count:35
Charpy Impact, Notched 0.400 - 4.50 J/cm²
1.90 - 21.4 ft-lb/in²
Average value: 1.23 J/cm² Grade Count:39
0.200 - 2.50 J/cm²

@Temperature -30.0 - 30.0 °C
0.952 - 11.9 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 0.832 J/cm² Grade Count:29
Thermal Properties Metric English Comments
CTE, linear 1.50 - 80.0 µm/m-°C
0.833 - 44.4 µin/in-°F
Average value: 23.9 µm/m-°C Grade Count:23
CTE, linear, Transverse to Flow 10.0 - 110 µm/m-°C
5.56 - 61.1 µin/in-°F
Average value: 66.2 µm/m-°C Grade Count:21
Melting Point 200 - 310 °C
392 - 590 °F
Average value: 260 °C Grade Count:44
Maximum Service Temperature, Air 90.0 - 250 °C
194 - 482 °F
Average value: 164 °C Grade Count:24
Deflection Temperature at 0.46 MPa (66 psi) 215 - 257 °C
419 - 495 °F
Average value: 239 °C Grade Count:11
Deflection Temperature at 1.8 MPa (264 psi) 70.0 - 285 °C
158 - 545 °F
Average value: 224 °C Grade Count:47
Deflection Temperature at 8.0 MPa 50.0 - 204 °C
122 - 399 °F
Average value: 141 °C Grade Count:20
Vicat Softening Point 230 - 252 °C
446 - 486 °F
Average value: 244 °C Grade Count:3
UL RTI, Electrical 65.0 - 140 °C
149 - 284 °F
Average value: 106 °C Grade Count:4
UL RTI, Mechanical with Impact 65.0 - 105 °C
149 - 221 °F
Average value: 81.0 °C Grade Count:4
UL RTI, Mechanical without Impact 65.0 - 140 °C
149 - 284 °F
Average value: 98.0 °C Grade Count:4
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:32
Oxygen Index 32.0 - 35.0 %
32.0 - 35.0 %
Average value: 33.5 % Grade Count:4
Glow Wire Test 650 - 960 °C
1200 - 1760 °F
Average value: 865 °C Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+10 - 1.00e+15 ohm-cm
1.00e+10 - 1.00e+15 ohm-cm
Average value: 1.43e+14 ohm-cm Grade Count:29
Surface Resistance 1.00e+10 - 1.00e+15 ohm
1.00e+10 - 1.00e+15 ohm
Average value: 4.88e+13 ohm Grade Count:23
Dielectric Strength 21.0 - 60.0 kV/mm
533 - 1520 kV/in
Average value: 31.3 kV/mm Grade Count:20
Dissipation Factor 0.0200
0.0200
Average value: 0.0200 Grade Count:4
Comparative Tracking Index 250 - 650 V
250 - 650 V
Average value: 534 V Grade Count:32
Hot Wire Ignition, HWI 120 sec
120 sec
Average value: 120 sec Grade Count:3
High Amp Arc Ignition, HAI 120 arcs
120 arcs
Average value: 120 arcs Grade Count:3
Processing Properties Metric English Comments
Nozzle Temperature 240 - 310 °C
464 - 590 °F
Average value: 279 °C Grade Count:7
Melt Temperature 225 - 310 °C
437 - 590 °F
Average value: 272 °C Grade Count:13
Mold Temperature 60.0 - 110 °C
140 - 230 °F
Average value: 83.9 °C Grade Count:12
Drying Temperature 79.4 - 90.0 °C
175 - 194 °F
Average value: 80.8 °C Grade Count:12
Moisture Content 0.0500 - 0.200 %
0.0500 - 0.200 %
Average value: 0.171 % Grade Count:5
1.40 - 1.90 %

@Temperature 70.0 - 70.0 °C
1.40 - 1.90 %

@Temperature 158 - 158 °F
Average value: 1.65 % Grade Count:4
Injection Pressure 34.5 - 138 MPa
5000 - 20000 psi
Average value: 88.7 MPa Grade Count:3