Polymer Property : Flexural Yield Strength = 8120 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	56.0 MPa	8120 psi	2 mm/min; ISO 178
SABIC Innovative Plastics GELOY CR3020 ASA Low-gloss ASA for profile and capstock applications
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Geloy XTWE265 ASA Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics GELOY XTWE265 ASA (Asia Pacific) Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Geloy XTWE265 ASA (Europe-Africa-Middle East) Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied..
Flexural Yield Strength	56.0 MPa	8120 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied..
Flexural Yield Strength	56.0 - 159 MPa	8120 - 23000 psi	Average value: 88.2 MPa Grade Count:49
Overview of materials for Polyphenylene Ether, Heat Resistant This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Heat Resistant". Each property range of values reported is minimum and maximum valu..
Flexural Yield Strength	56.0 MPa	8120 psi	ASTM D790
North Wood Plastics Polypropylene with 20% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc.
Flexural Yield Strength	56.0 MPa	8120 psi	ASTM D790
North Wood Plastics PS with 40% Wood Fiber Data provided by North Wood Plastics, Inc.
Flexural Yield Strength	56.0 - 115 MPa	8120 - 16700 psi	Average value: 87.0 MPa Grade Count:3
Overview of materials for Phenolic/Rubber; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of approp..
Flexural Yield Strength	56.0 - 275 MPa	8120 - 39900 psi	Average value: 205 MPa Grade Count:24
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl..
Flexural Yield Strength	56.0 MPa	8120 psi	ASTM D790
Hannam Chemical Hanalac 711 ABS, Plating Grade Plating grade with excellent moldability and easy to surface treat. It also has a strong adhesive strength after plating and an excellent heat cycle. Applications: Appliances, TV frames, automoti..
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 337 PBT Low temperature impact PBT. Automotive applications: underhood power distribution boxes and covers.
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked.
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WH0270F PBT LNP* Thermocomp* WH0270F is a dense compound based on PBT.
Flexural Yield Strength	56.0 MPa	8120 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP PB006EQ PA 6 (Europe-Africa-Middle East) LNP THERMOCOMP PB006EQ is a compound based on PA 6 containing Glass Bead. Added features include Reduced Moisture.
Flexural Yield Strength	56.0 MPa	8120 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp WH0270FX_WH5A289 PBT 2.7 specific gravity PBTThis data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	56.0 MPa	8120 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermotuf PX06093 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* PX06093 is a compound based on PA 6 resin containing Impact Modifier. Added features include: High Impact, UV-Stabilized, Laser Marking Grade.This data was supplied by SABIC-IP for t..
Flexural Yield Strength	56.0 MPa	8120 psi	2 mm/min; ISO 178
Eurostar Staramide PX06093 PA6, Impact Modified, Injection Molded Staramide PX06093 is an UV Stabilized, Impact Modified Polyamide 6 Injection Molding Resin (also known as P1000HI020UVL)Information provided by Eurostar.
Flexural Yield Strength	56.0 - 82.0 MPa	8120 - 11900 psi	Average value: 68.8 MPa Grade Count:19
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum..