LATI Latan 23UVE71 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer LATI
Trade Name Latan
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latan 23UVE71 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyoxymethylene (POM). UV stabilized. Toughened. Low viscosity. Good elongation and impact resistance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
Linear Mold Shrinkage, Flow 0.0225 - 0.0265 cm/cm
0.0225 - 0.0265 in/in
Linear Mold Shrinkage, Transverse 0.0225 - 0.0265 cm/cm
0.0225 - 0.0265 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Elongation at Break 90 %

@Temperature 23.0 °C
90 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
>= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
>= 100 %

@Temperature 194 °F
Tensile Modulus 0.800 GPa

@Temperature 90.0 °C
116 ksi

@Temperature 194 °F
1.40 GPa

@Temperature 60.0 °C
203 ksi

@Temperature 140 °F
2.70 GPa

@Temperature 23.0 °C
392 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 65.0 °C
149 °F
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Vicat Softening Point 130 °C

@Load 5.00 kg
266 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 175 - 200 °C
347 - 392 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa