Total PPC 3660 Polypropylene, Heterophasic Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Total Atofina |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPC 3660 Polypropylene, Heterophasic Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ATOFINA Polypropylene PPC 3660 is an heterophasic copolymer. PPC 3660 is characterized by a low fluidity hence good melt strength to provide east of processing and good manufactured article properties. ApplicationPPC 3660 is suitable particularly for the extrusion of corrugated cardboard, profiles and for extrusion-thermoforming applications where high impact resistance is required.Information provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.525 g/cc | 0.0190 lb/in³ | ISO 1183 |
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 77 | 77 | ISO 2039-2 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
| Elongation at Yield | 11 % | 11 % | ISO 527-2 |
| Tensile Modulus | 1.05 GPa | 152 ksi | ISO 527-2 |
| Flexural Modulus | 1.15 GPa | 167 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 179 |
| 7.00 kJ/m² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | NB | NB | ISO 179 |
| 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | 120°C per hour; ISO 75-2 |
| Vicat Softening Point | 60.0 °C | 140 °F | 50N-50°C per hour; ISO 306 |
| 130 °C | 266 °F | 10N-50°C per hour; ISO 306 |