Overview of materials for Nylon 12, 30% Glass Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 12, 30% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.17 - 1.96 g/cc
0.0423 - 0.0708 lb/in³
Average value: 1.28 g/cc Grade Count:41
Filler Content 25.0 - 30.0 %
25.0 - 30.0 %
Average value: 29.0 % Grade Count:5
Water Absorption 0.100 - 1.40 %
0.100 - 1.40 %
Average value: 0.765 % Grade Count:21
Moisture Absorption at Equilibrium 0.500 - 0.600 %
0.500 - 0.600 %
Average value: 0.569 % Grade Count:13
Water Absorption at Saturation 1.00 - 1.40 %
1.00 - 1.40 %
Average value: 1.16 % Grade Count:8
Linear Mold Shrinkage 0.00100 - 0.00700 cm/cm
0.00100 - 0.00700 in/in
Average value: 0.00290 cm/cm Grade Count:26
Linear Mold Shrinkage, Transverse 0.00500 - 0.0110 cm/cm
0.00500 - 0.0110 in/in
Average value: 0.00792 cm/cm Grade Count:13
Melt Flow 2.20 - 6.70 g/10 min
2.20 - 6.70 g/10 min
Average value: 4.57 g/10 min Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109 - 110
109 - 110
Average value: 110 Grade Count:4
Hardness, Shore D 77.0 - 83.0
77.0 - 83.0
Average value: 80.6 Grade Count:6
Ball Indentation Hardness 120 - 155 MPa
17400 - 22500 psi
Average value: 131 MPa Grade Count:7
Tensile Strength, Ultimate 60.0 - 140 MPa
8700 - 20300 psi
Average value: 110 MPa Grade Count:30
35.0 - 95.0 MPa

@Temperature 60.0 - 150 °C
5080 - 13800 psi

@Temperature 140 - 302 °F
Average value: 58.8 MPa Grade Count:2
Tensile Strength, Yield 69.0 - 130 MPa
10000 - 18900 psi
Average value: 105 MPa Grade Count:11
Elongation at Break 2.00 - 12.0 %
2.00 - 12.0 %
Average value: 5.45 % Grade Count:40
4.50 - 16.0 %

@Temperature 60.0 - 150 °C
4.50 - 16.0 %

@Temperature 140 - 302 °F
Average value: 9.38 % Grade Count:2
Elongation at Yield 3.00 - 6.50 %
3.00 - 6.50 %
Average value: 4.38 % Grade Count:4
>= 10.0 %

@Temperature 60.0 - 150 °C
>= 10.0 %

@Temperature 140 - 302 °F
Average value: 10.0 % Grade Count:1
Modulus of Elasticity 4.00 - 15.8 GPa
580 - 2290 ksi
Average value: 7.01 GPa Grade Count:36
2.10 - 7.20 GPa

@Temperature 60.0 - 150 °C
305 - 1040 ksi

@Temperature 140 - 302 °F
Average value: 4.04 GPa Grade Count:2
Flexural Yield Strength 134 - 185 MPa
19500 - 26800 psi
Average value: 156 MPa Grade Count:15
Flexural Modulus 4.00 - 7.10 GPa
580 - 1030 ksi
Average value: 5.52 GPa Grade Count:18
Compressive Yield Strength 68.9 MPa
10000 psi
Average value: 68.9 MPa Grade Count:3
Izod Impact, Notched 1.07 - 1.80 J/cm
2.00 - 3.37 ft-lb/in
Average value: 1.34 J/cm Grade Count:14
Izod Impact, Unnotched 5.34 - 5340 J/cm
10.0 - 10000 ft-lb/in
Average value: 7.32 J/cm Grade Count:9
Izod Impact, Notched (ISO) 10.0 - 17.0 kJ/m²
4.76 - 8.09 ft-lb/in²
Average value: 14.5 kJ/m² Grade Count:4
Charpy Impact Unnotched 4.50 - 10.0 J/cm²
21.4 - 47.6 ft-lb/in²
Average value: 7.98 J/cm² Grade Count:20
4.00 - 10.0 J/cm²

@Temperature -30.0 - 30.0 °C
19.0 - 47.6 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 7.89 J/cm² Grade Count:18
Charpy Impact, Notched 0.650 - 2.50 J/cm²
3.09 - 11.9 ft-lb/in²
Average value: 1.62 J/cm² Grade Count:20
0.800 - 2.10 J/cm²

@Temperature -30.0 - 30.0 °C
3.81 - 9.99 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 1.22 J/cm² Grade Count:18
Thermal Properties Metric English Comments
CTE, linear 20.0 - 80.0 µm/m-°C
11.1 - 44.4 µin/in-°F
Average value: 43.3 µm/m-°C Grade Count:21
CTE, linear, Transverse to Flow 50.0 - 150 µm/m-°C
27.8 - 83.3 µin/in-°F
Average value: 110 µm/m-°C Grade Count:9
Thermal Conductivity 0.160 - 0.432 W/m-K
1.11 - 3.00 BTU-in/hr-ft²-°F
Average value: 0.342 W/m-K Grade Count:3
Melting Point 165 - 185 °C
329 - 365 °F
Average value: 176 °C Grade Count:27
Maximum Service Temperature, Air 90.0 - 160 °C
194 - 320 °F
Average value: 129 °C Grade Count:10
Deflection Temperature at 0.46 MPa (66 psi) 138 - 182 °C
280 - 360 °F
Average value: 172 °C Grade Count:22
Deflection Temperature at 1.8 MPa (264 psi) 130 - 177 °C
266 - 351 °F
Average value: 162 °C Grade Count:31
Deflection Temperature at 8.0 MPa 90.0 - 125 °C
194 - 257 °F
Average value: 94.4 °C Grade Count:8
Vicat Softening Point 162 - 175 °C
324 - 347 °F
Average value: 171 °C Grade Count:11
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:33
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+15 ohm-cm
1000 - 1.00e+15 ohm-cm
Average value: 1.99e+14 ohm-cm Grade Count:22
Surface Resistance 1000 - 1.00e+15 ohm
1000 - 1.00e+15 ohm
Average value: 1.54e+14 ohm Grade Count:15
Dielectric Constant 3.40 - 4.10
3.40 - 4.10
Average value: 3.86 Grade Count:6
Dielectric Strength 17.7 - 45.0 kV/mm
450 - 1140 kV/in
Average value: 37.1 kV/mm Grade Count:16
Dissipation Factor 0.000345 - 0.0650
0.000345 - 0.0650
Average value: 0.0227 Grade Count:9
Comparative Tracking Index 575 - 600 V
575 - 600 V
Average value: 599 V Grade Count:16
Processing Properties Metric English Comments
Processing Temperature 216 - 266 °C
420 - 510 °F
Average value: 241 °C Grade Count:5
Melt Temperature 210 - 274 °C
410 - 525 °F
Average value: 231 °C Grade Count:5
Mold Temperature 60.0 - 104 °C
140 - 220 °F
Average value: 82.5 °C Grade Count:10
Drying Temperature 70.0 - 90.0 °C
158 - 194 °F
Average value: 79.8 °C Grade Count:5
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:7