Polymer Property : Deflection Temperature at 8.0 MPa = 194 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	>= 90.0 °C	>= 194 °F	ISO 175
Perstorp Compounds 161 Urea-Formaldehyde w/ cellulose filler Perstorp 161 compression grade has low shrinkage, low water absorption and high strength. It is suitable for circuit breakers and electrical accessories in humid environments.Information provided by..
Deflection Temperature at 8.0 MPa	>= 90.0 °C	>= 194 °F	ISO 175
Perstorp Compounds 171 Urea-Formaldehyde w/ cellulose filler Information provided by Perstorp Compounds Inc.
Deflection Temperature at 8.0 MPa	>= 90.0 °C	>= 194 °F	ISO 175
Perstorp Compounds 371 Urea-Formaldehyde w/ cellulose filler Information provided by Perstorp Compounds Inc.
Deflection Temperature at 8.0 MPa	>= 90.0 °C	>= 194 °F	ISO 175
Perstorp Compounds 136 Urea-Formaldehyde w/ cellulose filler A UF-based injection grade designed for hidden parts like sockets, circuit breakers, clamps, switches.Information provided by Perstorp Compounds Inc.
Deflection Temperature at 8.0 MPa	90.0 - 125 °C	194 - 257 °F	Average value: 94.4 °C Grade Count:8
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. ..
Deflection Temperature at 8.0 MPa	90.0 Â°C	194 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® AKV 30 G H2.0 SR1 900051 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, better surface than AKV 30 H2.0, good heat-ageing resistance
Deflection Temperature at 8.0 MPa	90.0 Â°C	194 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, suitable for GIT (gas assisted technology), good surface finish, good heat-ageing resistance
Deflection Temperature at 8.0 MPa	90.0 Â°C	194 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® BKV 130 000000 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30, even in..
Deflection Temperature at 8.0 MPa	90.0 Â°C	194 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® BKV 130 H3.0 101006 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30 H3.0, ev..
Deflection Temperature at 8.0 MPa	90.0 Â°C	194 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® BKV 330 H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding type, 30% glass fibers, branched/structural viscosity, good weldability (vibration or hot plate), good heat-ageing resistance
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® BGM-40 X PA6-(GF+MD)40 Product description: Grilon BGM-40 X is a heat stabilized PA 6 injection molding grade with a 40 % reinforcement combination (mineral and glass fiber). Grilon BGM-40 X has the following important pr..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LBV-30H FWA black 9225 PA12-GF30 Product Description: Grilamid LBV-30H FWA black 9225 is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined wit..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LV-3 ESD PA12-GF30 Product description: Grilamid LV-3 ESD is an antistatic PA12 injection molding grade, with fiber reinforcement of 30%. Due to its special formulation, the material can be used for applications where..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LV-30H FWA black 9225 PA12-GF30 Product description: Grilamid LV-30H FWA black 9225 is a 30 % glass fiber reinforced, heat stabilized polyamide12 injection molding grade with the following special features: Stiffness combined with..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LV-30H FWA nat PA12-GF30 Product description: Grilamid LV-30H FWA natural is a 30 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined with h..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LV-3A H PA12-GF30 Grilamid LV-3A H is a 30 % glass fibre reinforced PA12 for injection moulding. Grilamid LV-3A H is very stiff and tough and offers an improved hydrolysis resistance compared to standard PA12 GF 30.I..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LV-3H PA12-GF30 Product description: Grilamid LV-3H is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following product profile: very low water absorptionhigh dimensiona..
Deflection Temperature at 8.0 MPa	90.0 °C	194 °F	ISO 75-1/-2
EMS-Grivory Grivory® LBV-30H FWA nat PA12-GF30 Product Description: Grilamid LBV-30H FWA natural is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined with h..