- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 266 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 266 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | STN EN ISO 75/A |
| Plastcom SLOVALEN PH 51 T 40 Polypropylene Homopolymer, 40% Micronized Talc FeaturesModified homopolymer PP for injection moulding with the content of 40% micronized, floated, chemically modified talc. General application in all industry branches - packing material, garden.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Unannealed; ISO 75-2/A |
| PolyOne Trilliant™ HC HC6200-5001 XR Grey Polyamide 12 (Nylon 12) The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific) Cycoloy* C4220K resin is an injection moldable 20% glass reinforced non FR PC-ABS.
Key features include improved Knit Line strength, good flow, excellent strength & rigidity, heat resistance & hyd.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® EX1632T PC Lexan* EX1632T polycarbonate resin is designed for use in multi-wall sheet or profile extrusion applications. It contains branched polycarbonate resin, release, and UV stabilizer. It is available .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® PK2870 PC LEXAN* PK2870 polycarbonate resin, global grade, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, blow molding, high melt strength, high impact resistance, Available in transparent colors onl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics Lexan® PK2870 PC (Asia Pacific) LEXAN* PK2870 polycarbonate resin, global grade, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, blow molding, high melt strength, high impact resistance, Available in transparent colors onl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® PK2870 PC (Europe-Africa-Middle East) LEXAN* PK2870 polycarbonate resin, global grade, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, blow molding, high melt strength, high impact resistance, Available in transparent colors onl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 950A PC (Europe-Africa-Middle East) LEXAN 950A is a high viscosity flame retardant grade, especially suitable for electrical applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 955A PC (Europe-Africa-Middle East) Lexan* 955A Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating. Lexan 955A is available in transparen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| Asahi Kasei Tenac® 5012 Acetal Homopolymer
(discontinued **) Standard-flow grade, with reduced stiffness and increased elongation through addition of special polymers.Applications: Clips, fasteners, press-fit parts.This product is not a part of the standard p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | |
| Covestro Makrolon® 1239 Polycarbonate, Blow Molding/Extrusion Grade
(discontinued **) Pseudoplastic behavior and high viscosity extrusion and injection molding grade, BgVV- and FDA grade for food contact applications, high melt stability, better resistance to hot water, specially sui.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL-4036 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 130 °C | >= 266 °F | ISO 75-2 |
| Menzolit Menzolit® BMC 0170 Unsaturated Polyester UP BMC 0170 is a general purpose BMC for electrical applications. Product according to type 801 DIN 16911. The glass content is on a level that combines good mouldability with good strength and stiffne.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY HI1002ML PC, High Impact Description: Injection Molding, PC, General Purpose, High Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 9046-16-6Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 18 SR FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 19 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75/Af |
| Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY Description: TECHNYL® C 52G4 MZ25 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilized and is suitable for injection molding. This product is .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD0009P PC (Asia Pacific) LNP STAT-KON* DD0009P is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD0009PC PC (Europe-Africa-Middle East) LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® HN-1064 PC, Unreinforced FR PC material that is applied to other resin for mobile phone chargersInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® FD-1112 PC, FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON DD0009PC PC LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Valox® VX4910 ASA+PBT (Europe-Africa-Middle East) 10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP NF002 PC+ABS LNP THERMOCOMP* NF002 is a compound based on PC+ABS resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Covestro Makrolon® SF805 Polycarbonate, 5% Glass Filled MVR (300 °C/1.2 kg) 7.0 cm3/10 minStructural foam5 % Glass fiber reinforcedNormal fiberChlorine- and bromine-free flame retardantHigh viscosityEasy releaseInjection moldingAvailable in natural (opa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded Starflam PK0069 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin (also known as Starflam PA6 30E6 Z88)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| E-Polymers Tekaloy® G70GR , 30% Glass Reinforced PC/ABS Alloy 30% Glass Fiber reinforced, High stiffness, Dimensional stabilityInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0336G20CL Glass Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | |
| BASF Procom® D 1085 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| BLUESTAR LXS 314 G20 PPE-HIPS, 20% Glass Filled Typical Applications: Water industrial partsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||