Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | >= 90.0 °C | >= 194 °F | ISO 175 |
Perstorp Compounds 161 Urea-Formaldehyde w/ cellulose filler Perstorp 161 compression grade has low shrinkage, low water absorption and high strength. It is suitable for circuit breakers and electrical accessories in humid environments.Information provided by.. |
|||
Deflection Temperature at 8.0 MPa | >= 90.0 °C | >= 194 °F | ISO 175 |
Perstorp Compounds 171 Urea-Formaldehyde w/ cellulose filler Information provided by Perstorp Compounds Inc. |
|||
Deflection Temperature at 8.0 MPa | >= 90.0 °C | >= 194 °F | ISO 175 |
Perstorp Compounds 371 Urea-Formaldehyde w/ cellulose filler Information provided by Perstorp Compounds Inc. |
|||
Deflection Temperature at 8.0 MPa | >= 90.0 °C | >= 194 °F | ISO 175 |
Perstorp Compounds 136 Urea-Formaldehyde w/ cellulose filler A UF-based injection grade designed for hidden parts like sockets, circuit breakers, clamps, switches.Information provided by Perstorp Compounds Inc. |
|||
Deflection Temperature at 8.0 MPa | 90.0 - 125 °C | 194 - 257 °F | Average value: 94.4 °C Grade Count:8 |
Overview of materials for Nylon 12, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
Lanxess Durethan® AKV 30 G H2.0 SR1 900051 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, better surface than AKV 30 H2.0, good heat-ageing resistance |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
Lanxess Durethan® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, suitable for GIT (gas assisted technology), good surface finish, good heat-ageing resistance |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 130 000000 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30, even in.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 130 H3.0 101006 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30 H3.0, ev.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 330 H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding type, 30% glass fibers, branched/structural viscosity, good weldability (vibration or hot plate), good heat-ageing resistance |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® BGM-40 X PA6-(GF+MD)40 Product description: Grilon BGM-40 X is a heat stabilized PA 6 injection molding grade with a 40 % reinforcement combination (mineral and glass fiber). Grilon BGM-40 X has the following important pr.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LBV-30H FWA black 9225 PA12-GF30 Product Description: Grilamid LBV-30H FWA black 9225 is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined wit.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-3 ESD PA12-GF30 Product description: Grilamid LV-3 ESD is an antistatic PA12 injection molding grade, with fiber reinforcement of 30%. Due to its special formulation, the material can be used for applications where.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-30H FWA black 9225 PA12-GF30 Product description: Grilamid LV-30H FWA black 9225 is a 30 % glass fiber reinforced, heat stabilized polyamide12 injection molding grade with the following special features: Stiffness combined with.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-30H FWA nat PA12-GF30 Product description: Grilamid LV-30H FWA natural is a 30 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined with h.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-3A H PA12-GF30 Grilamid LV-3A H is a 30 % glass fibre reinforced PA12 for injection moulding. Grilamid LV-3A H is very stiff and tough and offers an improved hydrolysis resistance compared to standard PA12 GF 30.I.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-3H PA12-GF30 Product description: Grilamid LV-3H is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following product profile: very low water absorptionhigh dimensiona.. |
|||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LBV-30H FWA nat PA12-GF30 Product Description: Grilamid LBV-30H FWA natural is a 30% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: Stiffness combined with h.. |