BASF Ultraform N 2320 003 UNC Q600 POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	BASF
Trade Name	Ultraform N
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultraform N 2320 003 UNC Q600 POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultraform N 2320 003 UNC Q600 is a rapidly solidifying grade of POM for injection molding. Contains a mold release agent.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C/50% R.H.; ISO 62
Melt Flow	8.8 g/10 min @Load 2.16 kg, Temperature 190 °C	8.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	145 MPa	21000 psi	358/30; ISO 2039-1
Tensile Strength	60.0 MPa @Time 864000 sec	8700 psi @Time 240 hour	Hot water storage of tensile bars at 130°C in an autoclave
	61.0 MPa @Time 450000 sec	8850 psi @Time 125 hour	Hot water storage of tensile bars at 130°C in an autoclave
	66.0 MPa @Time 0.000 sec	9570 psi @Time 0.000 hour	Hot water storage of tensile bars at 130°C in an autoclave
Tensile Stress	5.00 MPa @Strain 0.500 %, Time 3.60e+7 sec	725 psi @Strain 0.500 %, Time 10000 hour	ISO 899-1
	7.00 MPa @Strain 0.500 %, Time 360000 sec	1020 psi @Strain 0.500 %, Time 100 hour	ISO 899-1
	10.0 MPa @Strain 0.500 %, Time 3600 sec	1450 psi @Strain 0.500 %, Time 1.00 hour	ISO 899-1
	15.0 MPa @Strain 2.00 %, Time 3.60e+7 sec	2180 psi @Strain 2.00 %, Time 10000 hour	ISO 899-1
	17.0 MPa @Strain 1.50 %, Time 360000 sec	2470 psi @Strain 1.50 %, Time 100 hour	ISO 899-1
	19.0 MPa @Time 3600 sec, Strain 1.00 %	2760 psi @Time 1.00 hour, Strain 1.00 %	ISO 899-1
	25.0 MPa @Strain 4.00 %, Time 3.60e+7 sec	3630 psi @Strain 4.00 %, Time 10000 hour	ISO 899-1
	29.0 MPa @Strain 3.00 %, Time 360000 sec	4210 psi @Strain 3.00 %, Time 100 hour	ISO 899-1
	31.0 MPa @Time 3600 sec, Strain 2.00 %	4500 psi @Time 1.00 hour, Strain 2.00 %	ISO 899-1
Tensile Strength, Yield	65.0 MPa	9430 psi	50mm/min; ISO 527
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO 527
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ISO 527
	60.0 MPa @Temperature 40.0 °C	8700 psi @Temperature 104 °F	ISO 527
Elongation at Break	27 %	27 %	50mm/min; ISO 527
Elongation at Yield	9.4 %	9.4 %	50mm/min; ISO 527
Modulus of Elasticity	2.70 GPa	392 ksi	ISO 527
	1.00 GPa @Temperature 80.0 °C	145 ksi @Temperature 176 °F	ISO 899-1
	1.90 GPa @Temperature 60.0 °C	276 ksi @Temperature 140 °F	ISO 899-1
	3.00 GPa @Temperature 20.0 °C	435 ksi @Temperature 68.0 °F	ISO 899-1
Tensile Modulus	2.41 GPa @Thickness 1.50 mm, Temperature 30.0 °C	350 ksi @Thickness 0.0591 in, Temperature 86.0 °F
	2.59 GPa @Thickness 4.00 mm, Temperature 30.0 °C	376 ksi @Thickness 0.157 in, Temperature 86.0 °F
	2.60 GPa @Thickness 1.50 mm, Temperature 90.0 °C	377 ksi @Thickness 0.0591 in, Temperature 194 °F
	2.71 GPa @Thickness 4.00 mm, Temperature 90.0 °C	393 ksi @Thickness 0.157 in, Temperature 194 °F
	2.79 GPa @Thickness 1.50 mm, Temperature 120 °C	405 ksi @Thickness 0.0591 in, Temperature 248 °F
	2.81 GPa @Thickness 4.00 mm, Temperature 120 °C	408 ksi @Thickness 0.157 in, Temperature 248 °F
Izod Impact, Notched (ISO)	5.50 kJ/m²	2.62 ft-lb/in²	ISO 180/A
	6.00 kJ/m²	2.86 ft-lb/in²	ISO 180/A
Charpy Impact Unnotched	21.0 J/cm²	99.9 ft-lb/in²	ISO 179
	19.0 J/cm² @Temperature -30.0 °C	90.4 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179
	0.550 J/cm² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	ISO 179
Tensile Creep Modulus, 1000 hours	1400 MPa	203000 psi	ISO 899

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	11.0 µm/m-°C @Temperature 23.0 - 55.0 °C	6.11 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	167 °C	333 °F
Deflection Temperature at 1.8 MPa (264 psi)	100 °C	212 °F	ISO 75
Vicat Softening Point	150 °C	302 °F	(50 °C/h / 50N) - B/50; ISO 306

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	3.8 @Frequency 100 Hz	3.8 @Frequency 100 Hz	IEC 60250
	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	40.0 kV/mm	1020 kV/in	IEC 60243-1
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Solution A; IEC 60112
	600 V	600 V	Test Solution B; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 230 °C	374 - 446 °F	Injection-molding
Mold Temperature	60.0 - 120 °C	140 - 248 °F

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
FDA	21 CFR 177.2470
Impact Modified	No
NSF Std. 51	Yes
NSF Std. 61	Yes
Primary Processing Technique	Injection Molding