Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
SABIC PP 504P Polypropylene Homopolymer for Raffia Applications Product Description: PP 504P is specially developed for producing stretched tapes with the following features:Consistent processabilityEasy orientationLow water carry overGood mechanical properties.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | |
Radici Radilon® A ESL128 (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Tensile Strength, Yield | 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
ASTM D638 |
BASF Capron® 8200 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
ISO 527 |
BASF Capron® 8202 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638-02 |
Ipiranga Petrochem PH 1721 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® B 35 FA 000000 Nylon 6, Film Grade PA 6, film , medium viscosity, lubricated, not nucleated, in compliance with FDA for food contact and acc. the German BgVV Recommendation XLIV, Section VI.A" Synthetic casings in polyamide"Applicati.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Europe-Africa-Middle East) Blow Moldable Impact modified XENOYThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PPX PPX7115F PPE+PP High modulus/impact/heat PPE+PP. Compliant with US FDA food contact regulations for temperatures of use of room temperature and below. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP LNP* THERMOCOMP* M7001XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additves. Designed for touch surfaces in patient critical healthcare applications. Added f.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
Teknor Apex Sinelec CCB2095 Specialty Polystyrene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Features: Electrically Conductive Forms: Pellets Processing Method: Injection MethodInformation Provided by Teknor Ape.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50mm/min; ISO 527-2 |
Borealis HK060AE Polypropylene Homopolymer HK060AE is a special low viscosity polypropylene homopolymer compound developed to fit the production of glass matt reinforced thermoplastics. This material is also suitable as base resin for the pr.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527-2 |
Total PPH 10042 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 10042 is a nucleated antistatic homopolymer. PPH 10042 is characterized by high fluidity for high speed injection of thin wall articles such as dairy pots and tubs, salad .. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527-2 |
Total PPH 3060 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 3060 is homopolymer.ApplicationATOFINA Polypropylene PPH 3060 is characterized by a low fluidity for continuous extrusion of strapping, rope fibers and high tenacity tapes .. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3476 is a homopolymer polypropylene for use in the process of multi-filaments, high tenacity continuous filament yarn and fine denier staple fibers. Information provided .. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® AS LF 20 PA66-Z20 Product description: Grilon AS LF 20 is a heat stabilized, normal viscosity PA 66 injection molding grade with 20% lubricant (PTFE + silicon oil). Grilon AS LF 20 has the following important propert.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000/58 CP Nylon 6, Impact Modified Until -40°C, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength, Yield | 35.0 MPa @Temperature 180 °C |
5080 psi @Temperature 356 °F |
ISO 527-1/-2 |
DSM Stanyl® TW341-J PA46 Heat Stabilized, Lubricated |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4181 black PA1010 Product description: Grilamid XE 4181 black 9992 is a unreinforced, high viscosity, plasticized, high impact resistant polyamide 1010 (PA1010) extrusion grade. Grilamid XE 4181 black 9992 is highly .. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
Braskem H 201 Fiber Extrusion Polypropylene Applications: Staple fibers for carpets and blankets; continuous filament for ropes, cords and rugs. Information provided by Braskem |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | |
BASF Novolen® 1100 L Polypropylene, Injection Molding Grade Injection molded parts, film tape, fibrillated film and monofilaments.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | |
BASF Novolen® 1102 H Polypropylene Grade with high processing stability for packaging tapes, film tape, fibrillated film, monofilaments, thermoformed and blow molded parts.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® C3U10 BK 23079 PA6/66 FR (Conditioned) Description: Flame-retardant injection-molding grade; light colorable. Burning behavior optimized for glow-wire requirements of IEC 60335. Typical applications are switches, housings, plug connector.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, Conditioned Vydyne® 41H BK03 is a general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vyd.. |
|||
Tensile Strength, Yield | 35.0 - 90.0 MPa | 5080 - 13100 psi | Average value: 65.7 MPa Grade Count:54 |
Overview of materials for Nylon 6, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum v.. |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | cond; ISO 527-1/-2 |
DSM Akulon® K225-KV PA6 FR(30) Flame Retardant (Halogen free), Heat stabilized |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527 |
Unipetrol PP MONSTEN® GB 003 Polypropylene Homopolymer Applications include injection molding, tapes, and thermoforming. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
Tensile Strength, Yield | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® L 25A NZ PA12-I Product Description: Grilamid L 25A NZ is a high viscosity extrusion grade Polyamide 12 (PA12). Grilamid L 25A NZ is hydrolysis and heat stabilized and impact modified. The main features of Grilamid.. |
|||
Tensile Strength, Yield | 35.0 - 60.0 MPa | 5080 - 8700 psi | Average value: 55.8 MPa Grade Count:6 |
Overview of materials for Polytrimethylene Terephthalate (PTT) This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val.. |