Polymer Property : Tensile Strength = 8700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength 60.0 MPa

@Temperature 23.0 °C
8700 psi

@Temperature 73.4 °F
DAM; ASTM D638
DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612  (Unverified Data**)
Zytel® 157HSL BK010 is a heat stabilized, weatherable, lubricated polyamide 612 resin that is suitable for molding and extrusion applications.Information provided by DuPont Performance Polymers
Tensile Strength 60.0 MPa

@Temperature 23.0 °C
8700 psi

@Temperature 73.4 °F
50%RH; ASTM D638
DuPont Performance Polymers Zytel® 7301 NC010 Nylon 6  (Unverified Data**)
Zytel® 7301 NC010 is a general purpose, unlubricated polyamide 6 resin for extrusion applications.Information provided by DuPont Performance Polymers
Tensile Strength 60.0 MPa

@Temperature 100 °C
8700 psi

@Temperature 212 °F
ISO 527
BASF Ultradur B 4300 G4 20% Glass Filled PBT
Ultradur B4300 G4 is an easy flowing injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small..
Tensile Strength 60.0 MPa

@Temperature 50.0 °C
8700 psi

@Temperature 122 °F
ISO 527
BASF Ultradur® S 4090 G2 10% Glass Filled PBT
Description: Is a PBT + ASA, easy-flowing injection-molding grades with 10% glass fibers; for rigid, tough and dimensionally stable technical parts e. g. housings, consoles, contact carriers, covers..
Tensile Strength 60.0 MPa

@Time 864000 sec
8700 psi

@Time 240 hour
Hot water storage of tensile bars at 130°C in an autoclave
BASF Ultraform N 2320 003 UNC Q600 POM
Ultraform N 2320 003 UNC Q600 is a rapidly solidifying grade of POM for injection molding. Contains a mold release agent.
Tensile Strength 60.0 MPa

@Strain 2.00 %,
Temperature 60.0 °C
8700 psi

@Strain 2.00 %,
Temperature 140 °F
50mm/min
BASF Ultramid® KR 4350 PA6/6T (Dry)
Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain con..
Tensile Strength 60.0 MPa

@Strain 6.00 %,
Temperature 150 °C
8700 psi

@Strain 6.00 %,
Temperature 302 °F
5mm/min
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry)
Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Tensile Strength 60.0 MPa

@Temperature 100 °C
8700 psi

@Temperature 212 °F
ISO 527
BASF Ultradur S 4090 G4 20% Glass Filled PBT
Ultradur S 4090 G4 is a 20% glass reinforced PBT+ASA blend. It produces moldings with good surface finish,is resistant to chemicals and stress cracking, and has low shrinkage and warpage.Applicatio..
Tensile Strength 60.0 MPa

@Strain 2.00 %,
Temperature 120 °C
8700 psi

@Strain 2.00 %,
Temperature 248 °F
ISO 527
BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry)
Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el..