Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | |
Polycasa Acryl® G 88 Acrylic Glazing, domed roof lights, lighting covers, publicity lighting, reflectors, lenses, instrument covers, dishes and bowls; mostly used in the automotive industry.Data was collected by ISO methods.Qui.. |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 |
Lanxess Pocan® B 1300 000000 PBT PBT, non-reinforced, injection molding, extrusion |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 |
Lanxess Pocan® B 1305 000000 PBT PBT, non-reinforced, injection molding |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 |
Lanxess Pocan® KU 1-7301 000000 PBT PBT, non-reinforced, injection molding, food contact |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 |
Lanxess Pocan® KU 2-7003 000000 PBT PBT, non-reinforced, injection molding |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 |
Lanxess Pocan® KU 2-7503/1 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa @Strain <=0.500 % |
203000 psi @Strain <=0.500 % |
ISO 899-1 |
Styrolution Luran® S 757 R Colored ASA Description: General-purpose grade for injection molding with high stiffness.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899 |
Styrolution Luran® S 767KE ASA Luran S 767KE is particular suitable for co-extrusion with PVC at low temperature. Hereby, it provides a glossy surface finish.Enhanced flowabilitySuitable for co-extrusion with PVCEnables high glos.. |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899 |
Styrolution Luran® S 777 K ASA Luran S 777 K is an easy flowing injection molding ASA grade with good toughness and heat distorsion resistance. |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa @Strain <=0.500 % |
203000 psi @Strain <=0.500 % |
ISO 899-1 |
Styrolution Luran® S 777 K UV Black 56625 ASA Description: Easy flowing injection molding grade with good toughness and heat distortion resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899 |
BASF Ultraform N 2320 003 UNC Q600 POM Ultraform N 2320 003 UNC Q600 is a rapidly solidifying grade of POM for injection molding. Contains a mold release agent. |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899 |
BASF Ultraform N 2320 U03 UNC Q600 POM Ultraform N2320 U03 UNC Q600 is a rapidly freezing UV stabilized general-purpose injection molding grade. |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa @Strain <=0.500 % |
203000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultraform® N2770 K POM Description: Is a POM, injection-molding grade with improved wear characteristics for sliding elements.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | |
Arkema Group Oroglas® VS-UVT Acrylic, Injection Molding Grade
(discontinued **) The outstanding flow of OROGLAS VS-UVT makes it as the material of choice for injection molding of part with thin wall thickness.The ultraviolet transmitting ( uvt) formulation is developed to meet .. |