Carpenter AerMet® 100 Aged at 900°F
| Category | Metal , Ferrous Metal , Alloy Steel , Tool Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | AerMet® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter AerMet® 100 Aged at 900°F.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
An alloy providing high hardness and strength combined with exceptional ductility and toughness. This alloy should be considered for aircraft and aerospace structural components requiring high strength, high fracture toughness and exceptional stress corrosion cracking resistance. AerMet 100 may be considered for use up to about 800°F (427°C). This alloy is not subject to the same restrictions as AF1410, thus may be considered a substitute.UNS K92580
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.89 g/cc | 0.285 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1980 MPa | 287000 psi | |
| Tensile Strength, Yield | 1700 MPa | 246000 psi | |
| Elongation at Break | 16.1 % | 16.1 % | |
| Reduction of Area | 67.3 % | 67.3 % | |
| Tensile Modulus | 194 GPa | 28200 ksi | |
| Fatigue Strength | 945 MPa @# of Cycles 1.00e+7 |
137000 psi @# of Cycles 1.00e+7 |
R=-1, Kt=1 |
| Fracture Toughness | 131.9 MPa-m½ | 120.0 ksi-in½ | |
| Charpy Impact | 47.5 J | 35.0 ft-lb | notched |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.23 % | 0.23 % | |
| Chromium, Cr | 3.1 % | 3.1 % | |
| Cobalt, Co | 13.4 % | 13.4 % | |
| Iron, Fe | 70.97 % | 70.97 % | |
| Molybdenum, Mo | 1.2 % | 1.2 % | |
| Nickel, Ni | 11.1 % | 11.1 % |