- Polymer Property : Tensile Strength, Yield = 3630 psi
Polymer Property : Tensile Strength, Yield = 3630 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ASTM D638 |
| Ovation Polymers Nemcon™ E HDPE 11000 HDPE HDPE-ESD Range Conductivity with improved processability and UV resistance.Information provided by Ovation Polymers |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| North Wood Plastics 60 PP + UNIFILL (20% Wood Fiber) Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 2.0 in/min; ASTM D638 |
| Ineos Nova 765 High Performance Styrenic Enhanced Polystyrene
(discontinued **) High flow, High impact, Color stable, Custom colorsApplications: High flow, multi-purpose injection molding grade where color stability is a requirement, Toys, Appliance, Computer peripheralsPerform.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | |
| LyondellBasell Lupolen® 5236 HX HDPE, Impact Grade Medium flow, impact resistant, high stress-crack resistant grade for closures for bottles that contain carbonated liquids. This product contains a slip agent.Data was collected by ISO methods and o.. |
|||
| Tensile Strength, Yield | >= 25.0 MPa | >= 3630 psi | |
| Kazanorgsintez PE2NT21-13 High Density Polyethylene Composite Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended for injection molding processin.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | Crosshead speed - 2"min.; ASTM D638 |
| LyondellBasell Alathon® ETP H4837 High Density Polyethylene ApplicationsALATHON H 4837 is a high-flow “freezer†grade resin that exhibits enhanced cold temperature impact performance, enhanced processability and thermal stability, with good color a.. |
|||
| Tensile Strength, Yield | 25.0 MPa @Temperature 22.0 °C |
3630 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® BMC 3100 Unsaturated Polyester UP BMC 3100 is a special BMC suitable for the use in head lamp reflectors. Because of its high temperature resistance and dimensional stability as well as low coefficient of thermal expansion, complex .. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| LG Chemical LUPOL GP-3152F General Purpose Polypropylene, 15% Mineral Fillers, High Impact, Flame Retardant LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON MX01739C PP LNP* SAT-KON* MX01739C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| SPS Guang Zhou FILLMAâ„¢ 5002F30C Mineral Filled Polypropylene Characteristic: 30%wt of Sulfate Calcium filled, low odor, good glossApplications: Household appliance parts, office suppliesInformation Provided by SPS (Guang Zhou) Ltd. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | At 50 mm/min; ISO 527-2 |
| Borealis Borcoat™ BB700E-7032 Polypropylene Compound for Steel Pipe Coating Applications Borcoat BB700E-7032 is a grey colored high impact polypropylene. This product is especially designed for direct extrusion of syntactic PP with high thermal insulations capacity and high compression.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | At 50 mm/min; ISO 527-2 |
| Borealis Bormed™ BE860MO Polypropylene Copolymer for Healthcare Applications Bormed BE860MO is a heterophasic copolymer characterized by an excellent impact strength also at low temperatures (deep freeze applications) together with high stiffness and good flow properties.Bor.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Unipetrol PE HD LITEN® BB 38 HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Total Lumicene® mPE M5220 Metallocene High Density Polyethylene This product is a Total Ecosolutions grade.Lumicene® mPE M 5220 is a High Density Polyethylene with very good organoleptic properties, dimensional stability, stress-cracking resistance, rigidity an.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | at max load; ASTM D638 |
| A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 |
| Borealis RA130E-2492 Polypropylene Random Copolymer RA130E-2492 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is dark blue colored. Applications: domestic water, heating, relining, plumbing, and in.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 572-2 |
| Total PPR 3261 Random Copolymer Polypropylene, Extrusion Grade Polypropylene PPR 3261 is a high melt strength random copolymer polypropylene with a melt flow index of 1.8 g/10 min suitable for extrusion applications.Information provided by Total Petrochemicals... |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM-D638 |
| Polyram RamOfin PPC501 Polypropylene, Flame Retardant Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | parallel; ISO 527-3 |
| Covestro Desmopan® DP 1970AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin Starpylen MB006SU is a Glass Bead Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® L 22A W 40 X PA12-I Product Description: Grilamid L 22A W 40 X is a flexible plasticized and impact modified heat and light stabilized Polyamide 12 (PA12). The main features of Grilamid L 22A W 40 X are: Good impact st.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO R 527 |
| Addiplast Addilene J 220 M20 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
| Tensile Strength, Yield | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ASTM Test |
| BASF Ultramid® 8253 HS PA6 (Dry) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM-D638 |
| Braskem Symbios 4102 Polypropylene Terpolymer Braskem Symbios 4102 is a medium melt flow rate terpolymer with a heat seal temperature below 120ºC on its treated face. It is designed for use as a heat sealing layer on bioriented films (BOPP) an.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ASTM D638 |
| Carmel Olefins CAPILENE® QT 73 A Propylene Random Copolymer Description: CAPILENE® QT 73 A is a clarified and antistatic additivated polypropylene random copolymer with a high melt flow rate, intended for injection molding of clear articles. It exhibits g.. |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| IRPC Polimaxx Polene 2563PCX TA6 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 30% TALCUM REINFORCED HIGH IMPACT STRENGTH, CONTAIN UV STABILIZER ADDITIVEAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES |
|||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 75HF Nylon 66/6, Heat Stabilized, Conditioned Vydyne® 75HF is a medium-high-viscosity, heat-stabilized PA66/6 copolymer resin designed for extrusion applications. It is available in natural color only. Vydyne 75HF resin offers a well-balanced .. |
|||