Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ASTM D638 |
Ovation Polymers OpteSTAT™ NC PC 1020 Polycarbonate based Carbon Nanotube Compound Material resistivity can be tailored to the application, while retaining the physical and thermal properties of the base polymer. Applications include components of disk drives, business machines or.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.2mm and 5VB at 1... |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.2mm and 5VB at 1... |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CX7720 PC+ABS (Asia Pacific) Cycoloy resin CX7720 is a non brominated and non chlorinated flame retardant PC/ABS resin grade featuring high heat resistance and thin wall FR. It is UL-94 listed at 1.2 mm V0 and 1.5mm 5VB. Its hi.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXD2034 PC (Europe-Africa-Middle East) LEXAN FXD2034 is a translucent medium viscosity flame retardant grade for light diffusion applications. The material is UV-stabilized. Can meet I2 rating according NF F16101.This data was supplied b.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPH4504 PPC (Asia Pacific) High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 of USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML6430 PC Copolymer (Asia Pacific) Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX1432D PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® SLX1432T PC Copolymer (Asia Pacific) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in transparent and tinted colors. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX2231D PC Copolymer (Asia Pacific) Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Diffusion colors.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPH4404 PPC+PC High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | |
Covestro Apec® DP 1-9339/5 Polycarbonate
(discontinued **) Key Features:Release agentUnfilledSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP COLORCOMP DX98550H PC LNP* COLORCOMP* DX98550H is an unfilled Polycarbonate resin. Added features of this grade are: Low Extractable, Healthcare. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl PKN4766 PPE+HIPS (Europe-Africa-Middle East) NORYL PKN4766 is a translucent PPO+PS extrusion grade for dilution with polystyrene resin. It is suitable for (microwavable) food packaging and is compliant with US and European food contact regulat.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527 |
Polyram RamOfin PPH501G4 Polypropylene, 20% Glass Fiber, Flame Retardant Glass fiber 20% reinforced, halogen free, flame retardant polypropylene for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
Polyram RamTal PM7002 Acetal, UV Stabilized UV stabilized acetal copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
Polyram RamTough PZ740 Polycarbonate, UV Stabilized UV stabilized low viscosity polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
Polyram RamTal PM1003 Acetal, General Purpose General purpose polyacetal copolymer for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D 638 |
Cossa Polimeri ESTACARB 2060 V0 Flame Retardant Polycarbonate Flame retardant class V0, antimony and PBDE free, opaque, high melt flow, high impact strength, high thermal resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | |
Covestro Apec® HT KU 1-9361 High-Heat Polycarbonate Transparent and opaque shades possible.Applications: Lighting, automotive and household goods, light covers.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated .. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527-1,-2 |
Covestro Bayblend® ET3036 FR PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Extru.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527-1,-2 |
Covestro Makrolon® 2258 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000/42 CP Nylon 6, Polymer Modified, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
Chi Mei Wonderlite® PC-110L Polycarbonate - UV Stabilized Head Lamp |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
Chi Mei Wonderlite® PC-110N Polycarbonate - Flame Retardant Opaque |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527-1 |
Barlog Plastics KEBAFORM C 270 LS black POM Copolymer unreinforced, laser markable POMInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D638 |
Ashley Polymers Ashlene® RH190H2-B Acetal General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. UV stabilized with carbon black for outstanding weatherability.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® SC652 NC010 Acetal (POM)
(Unverified Data**) Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for the Healthcare Industry Delrin SC652 is a medium viscosity acetal homopolymer with an advanced system of l.. |