Overview of materials for Nylon 66, 30% Carbon Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, 30% Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Carbon Fiber Filled". Specific grades with carbon fiber content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.20 - 1.57 g/cc
0.0434 - 0.0567 lb/in³
Average value: 1.29 g/cc Grade Count:32
Filler Content 25.0 - 30.0 %
25.0 - 30.0 %
Average value: 29.2 % Grade Count:13
Water Absorption 0.400 - 2.40 %
0.400 - 2.40 %
Average value: 0.763 % Grade Count:12
Moisture Absorption at Equilibrium 1.70 - 2.30 %
1.70 - 2.30 %
Average value: 1.94 % Grade Count:5
Water Absorption at Saturation 4.50 - 7.00 %
4.50 - 7.00 %
Average value: 5.67 % Grade Count:3
Linear Mold Shrinkage 0.000200 - 0.0150 cm/cm
0.000200 - 0.0150 in/in
Average value: 0.00252 cm/cm Grade Count:28
Linear Mold Shrinkage, Transverse 0.00480 - 0.0120 cm/cm
0.00480 - 0.0120 in/in
Average value: 0.00765 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Hardness, Rockwell R 97.0 - 120
97.0 - 120
Average value: 116 Grade Count:7
Tensile Strength, Ultimate 137 - 300 MPa
19900 - 43500 psi
Average value: 217 MPa Grade Count:30
65.0 - 260 MPa

@Temperature -40.0 - 150 °C
9430 - 37700 psi

@Temperature -40.0 - 302 °F
Average value: 130 MPa Grade Count:4
Elongation at Break 1.00 - 4.00 %
1.00 - 4.00 %
Average value: 2.23 % Grade Count:30
2.30 - 5.00 %

@Temperature 60.0 - 150 °C
2.30 - 5.00 %

@Temperature 140 - 302 °F
Average value: 3.58 % Grade Count:3
Modulus of Elasticity 16.0 - 33.1 GPa
2320 - 4800 ksi
Average value: 21.6 GPa Grade Count:25
4.90 - 21.5 GPa

@Temperature 60.0 - 150 °C
711 - 3120 ksi

@Temperature 140 - 302 °F
Average value: 11.4 GPa Grade Count:3
Flexural Yield Strength 215 - 420 MPa
31200 - 60900 psi
Average value: 320 MPa Grade Count:24
140 - 337 MPa

@Temperature -40.0 - 80.0 °C
20300 - 48900 psi

@Temperature -40.0 - 176 °F
Average value: 252 MPa Grade Count:1
Flexural Modulus 0.0000193 - 29.0 GPa
0.00280 - 4200 ksi
Average value: 16.1 GPa Grade Count:25
7.20 - 19.0 GPa

@Temperature -40.0 - 80.0 °C
1040 - 2760 ksi

@Temperature -40.0 - 176 °F
Average value: 13.4 GPa Grade Count:1
Compressive Yield Strength 152 - 172 MPa
22000 - 25000 psi
Average value: 164 MPa Grade Count:4
Izod Impact, Notched 0.534 - 2.40 J/cm
1.00 - 4.50 ft-lb/in
Average value: 1.31 J/cm Grade Count:18
0.720 - 0.800 J/cm

@Temperature -40.0 - -40.0 °C
1.35 - 1.50 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.760 J/cm Grade Count:1
Izod Impact, Unnotched 6.41 - 10.7 J/cm
12.0 - 20.0 ft-lb/in
Average value: 8.45 J/cm Grade Count:13
Izod Impact, Notched (ISO) 6.50 - 10.0 kJ/m²
3.09 - 4.76 ft-lb/in²
Average value: 8.09 kJ/m² Grade Count:4
6.00 - 7.00 kJ/m²

@Temperature -40.0 - -20.0 °C
2.86 - 3.33 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 6.50 kJ/m² Grade Count:1
Charpy Impact Unnotched 2.30 - 9.00 J/cm²
10.9 - 42.8 ft-lb/in²
Average value: 5.30 J/cm² Grade Count:10
2.10 - 8.50 J/cm²

@Temperature -40.0 - -20.0 °C
9.99 - 40.5 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 4.82 J/cm² Grade Count:4
Charpy Impact, Notched 0.500 - 1.80 J/cm²
2.38 - 8.57 ft-lb/in²
Average value: 0.945 J/cm² Grade Count:10
0.500 - 1.00 J/cm²

@Temperature -40.0 - -20.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 0.800 J/cm² Grade Count:3
Dart Drop, Total Energy 6.19 - 12.2 J

@Temperature -20.0 - -20.0 °C
4.57 - 9.00 ft-lb

@Temperature -4.00 - -4.00 °F
Average value: 9.19 J Grade Count:1
6.19 - 12.2 J

@Thickness 3.18 - 3.18 mm
4.57 - 9.00 ft-lb

@Thickness 0.125 - 0.125 in
Average value: 9.19 J Grade Count:1
Thermal Properties Metric English Comments
CTE, linear 6.00 - 25.0 µm/m-°C
3.33 - 13.9 µin/in-°F
Average value: 16.4 µm/m-°C Grade Count:8
Melting Point 221 - 263 °C
430 - 505 °F
Average value: 256 °C Grade Count:11
Maximum Service Temperature, Air 105 - 130 °C
221 - 266 °F
Average value: 124 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 240 - 260 °C
464 - 500 °F
Average value: 257 °C Grade Count:14
Deflection Temperature at 1.8 MPa (264 psi) 230 - 260 °C
446 - 500 °F
Average value: 251 °C Grade Count:26
Vicat Softening Point 230 - 255 °C
446 - 491 °F
Average value: 246 °C Grade Count:7
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:15
Electrical Properties Metric English Comments
Electrical Resistivity 0.0100 - 200000 ohm-cm
0.0100 - 200000 ohm-cm
Average value: 13200 ohm-cm Grade Count:17
Surface Resistance 10.0 ohm - 1e+05
10.0 ohm - 1e+05
Average value: 5190 ohm Grade Count:9
Processing Properties Metric English Comments
Processing Temperature 270 - 300 °C
518 - 572 °F
Average value: 284 °C Grade Count:5
Melt Temperature 260 - 320 °C
500 - 608 °F
Average value: 286 °C Grade Count:18
Mold Temperature 60.0 - 140 °C
140 - 284 °F
Average value: 88.2 °C Grade Count:23
Drying Temperature 75.0 - 107 °C
167 - 225 °F
Average value: 85.1 °C Grade Count:16
Moisture Content 0.150 - 0.200 %
0.150 - 0.200 %
Average value: 0.188 % Grade Count:10
Dew Point -28.9 - -17.8 °C
-20.0 - 0.000 °F
Average value: -19.6 °C Grade Count:6
Injection Pressure 30.0 - 124 MPa
4350 - 18000 psi
Average value: 93.1 MPa Grade Count:13