Polymer Property : Flexural Modulus = 19.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	16.0 - 19.0 GPa	2320 - 2760 ksi	Injection and Compression; ISO 178
Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excel..
Flexural Modulus	16.0 - 19.0 GPa	2320 - 2760 ksi	Injection; ISO 178
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Flexural Modulus	11.7 - 19.0 GPa	1700 - 2760 ksi	Average value: 14.6 GPa Grade Count:12
Overview of materials for Epoxy, Encapsulating, Glass or Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Glass or Mineral Filled". Each property range of values reported is minimum and ma..
Flexural Modulus	7.53 - 19.0 GPa	1090 - 2760 ksi	Average value: 11.5 GPa Grade Count:3
Overview of materials for Phenolic; Unreinforced; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic; Unreinforced; Molded". Each property range of values reported is minimum and maximum values of..
Flexural Modulus	6.70 - 19.0 GPa	972 - 2760 ksi	Average value: 8.15 GPa Grade Count:19
Overview of materials for Phenolic, Novolac, Impact Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Impact Grade, Filled". Each property range of values reported is minimum and maximum ..
Flexural Modulus	7.20 - 19.0 GPa @Temperature -40.0 - 80.0 °C	1040 - 2760 ksi @Temperature -40.0 - 176 °F	Average value: 13.4 GPa Grade Count:1
Overview of materials for Nylon 66, 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Carbon Fiber Filled". Specific grades with carbon fiber content between 25% and 34% are in..
Flexural Modulus	14.0 - 19.0 GPa	2030 - 2760 ksi	ISO 178
Vyncolit 3640 CG Novolac Phenolic Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..