Polymer Property : Tensile Strength, Ultimate = 9430 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	>= 65.0 MPa	>= 9430 psi	ISO 527; ASTM D638
Quadrant EPP Monocast® MC 904P Nylon for Pile Driver Pads (ASTM Product Data Sheet) Pile driver pads are used to prevent damage to the pile and the piling hammer. Fillers are usually made of hardwood - Azobe, for example. The disadvantage of Azobe is the 30-40% energy loss and it..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D638
Plaskolite Polycarbonate Mirror Sheet Better strength, security, and flame resistance than PETG mirror sheet.Data provided by the manufacturer, Plaskolite, Inc.
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D651
Resinoid 7051 Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Tensile Strength, Ultimate	65.0 - 131 MPa	9430 - 19000 psi	Average value: 93.0 MPa Grade Count:3
Overview of materials for Polyarylsulfone (PAS), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyarylsulfone; Molded/Extruded". Each property range of values reported is minimum and maximum values ..
Tensile Strength, Ultimate	65.0 - 74.1 MPa	9430 - 10800 psi	Average value: 71.0 MPa Grade Count:3
Overview of materials for Polyphenylene Ether, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Mineral Filled". Each property range of values reported is minimum and maximum valu..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PPE 1462 (discontinued **) PRE-ELEC PPE 1462 is a conductive thermoplastic compound based on modified polyphenylene ether (PPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electric..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
LATI LATILUB 73/13-01M Polyoxymethylene Base (POM), 1% Molybdenum Disulfide Self Lubricating Plastic (Unv Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri..
Tensile Strength, Ultimate	65.0 - 75.0 MPa	9430 - 10900 psi	Average value: 68.7 MPa Grade Count:16
Overview of materials for Polycarbonate, Gamma Radiation Resistant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Gamma Radiation Resistant". Each property range of values reported is minimum and maximum..
Tensile Strength, Ultimate	65.0 - 115 MPa @Temperature 60.0 - 120 °C	9430 - 16700 psi @Temperature 140 - 248 °F	Average value: 92.5 MPa Grade Count:2
Overview of materials for Polycarbonate, Carbon Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v..
Tensile Strength, Ultimate	65.0 - 197 MPa	9430 - 28500 psi	Average value: 107 MPa Grade Count:5
Overview of materials for Nylon 46, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Tensile Strength, Ultimate	65.0 - 342.669 MPa @Temperature -40.0 - 150 °C	9430 - 49700.1 psi @Temperature -40.0 - 302 °F	Average value: 128 MPa Grade Count:9
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. ..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D638
Lucky IF-870 Acrylic, High Flow Grade High flow for thin-walled injection molded parts and parts with long flow paths. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistanc..
Tensile Strength, Ultimate	65.0 MPa	9430 psi
Haysite ETR-FR-C Glass Reinforced Polyester Sheet, Electrical Grade (GPO3) ETR-FR-C meets NEMA GPO-3 requirements and exceeds NEMA in dielectric strength, arc resistance, and track resistance. This U.L. recognized grade is highly flame retardant and low smoke generating. E..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D638
Sumitomo Bakelite DurezÂ® 29502 B Phenolic, Compression Grade Durez 29502 B brown phenolic is a two stage, glass and mineral filled, special purpose molding material with improved mechanical and heat resistant properties. It is formulated for close tolerance ..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D638
Plenco 00755 Melamine-Phenolic, Granular, Injection Molded PLENCO 00755 is a melamine-phenolic copolymer molding compound offering excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 00755..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527-93
Wellman EcoLon® MRGF1619-WBK1 Mineral and Glass Reinforced Recycled Nylon 66 Description: Post Consumer Nylon Compound; WeatherableInformation provided by Wellman.
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
Wellman Wellamid® FR22F-N Flame Retardant Nylon 66, Lubricated Typical Applications: Electrical terminal blocks, electric fan switch housings, coil forms, multi-pin electrical connectors, electric fan switch housings, TV tuner components, automotive switch hous..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
Wellman Wellamid® GS25-66 22LH-N 25% Glass Sphere Filled Nylon 66, Lubricated & Heat Stabilized Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
Wellman Wellamid® MRT1487-N Mineral Reinforced Nylon 66, Lubricated & Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	dry; ISO 527-1/-2
DSM Akulon® K222-KMV5 /A PA6-MD25 FR(30) 25% Mineral Reinforced, Flame Retardant (Halogen free), Color Stabilized
Tensile Strength, Ultimate	65.0 MPa	9430 psi	cond; ISO 527-1/-2
DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30 10% Glass Reinforced, 20% Mineral Reinforced, Heat Stabilized
Tensile Strength, Ultimate	65.0 MPa	9430 psi	dry; ISO 527-1/-2
DSM EcoPaXX® Q-X07290 PA410-I Impact Modified
Tensile Strength, Ultimate	65.0 MPa	9430 psi
BASF Procom® D 1085 Polypropylene Data was collected by ISO methods and provided by BASF.
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ATSM D638
Ashley Polymers Ashlene® 69MG Nylon 66, Glass/Mineral reinforced A glass/mineral reinforced high flow Nylon 66 with exceptional dimensional stability.Data provided by the manufacturer
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D638
A. Schulman ComAlloy Comtuf® 651 Nylon 6, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.35% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
Tensile Strength, Ultimate	65.0 MPa @Temperature 1204 °C	9430 psi @Temperature 2199 °F
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ISO 527
Sumitomo Bakelite North America RX® 865M Fiberglass Reinforced Phenolic Novolac RX 865M is a fiberglass reinforced phenolic novolac compound, featuring dimensional stability, moderate impact resistance, and good strength and modulus.Information supplied by Sumitomo Bak North Am..
Tensile Strength, Ultimate	65.0 - 230 MPa @Temperature -40.0 - 200 °C	9430 - 33400 psi @Temperature -40.0 - 392 °F	Average value: 98.0 MPa Grade Count:4
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate	65.0 MPa	9430 psi	ASTM D651
Resinoid 7051 SS Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance