Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good StiffnessHigh Rigidity LubricatedNucleatedUses:BearingsCamsConnectorsFastenersGeneral PurposeHousings Industrial ApplicationsAppearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
 1.2 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Diameter 2.00 mm
 0.014 in/in

@Diameter 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
 0.016 in/in

@Diameter 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527-2
Tensile Strength, Yield 95.0 MPa
13800 psi
ISO 527-2
Elongation at Break 13 %
13 %
ISO 527-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-2
Tensile Modulus 3.80 GPa
551 ksi
ISO 527-2
Flexural Strength 100 MPa
14500 psi
ISO 178
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
6.00 kJ/m²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 130 °C

@Thickness 0.710 mm
 266 °F

@Thickness 0.0280 in
 UL 746
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.710 mm
 167 °F

@Thickness 0.0280 in
 UL 746
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
 UL 746
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.710 mm
 185 °F

@Thickness 0.0280 in
 UL 746
85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
 UL 746
85.0 °C

@Thickness 3.00 mm
 185 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-2

@Thickness 0.710 mm
 V-2

@Thickness 0.0280 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
Oxygen Index 26 %
26 %
ISO 4589-2
Glow Wire Test 700 °C

@Thickness 0.710 mm
 1290 °F

@Thickness 0.0280 in
 Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
800 °C

@Thickness 0.710 mm
 1470 °F

@Thickness 0.0280 in
 Flammability Index; IEC 60695-2-12
800 °C

@Thickness 1.50 mm
 1470 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
930 °C

@Thickness 3.00 mm
 1710 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 26.0 kV/mm

@Thickness 1.00 mm
 660 kV/in

@Thickness 0.0394 in
 IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
 120 - 179 sec

@Thickness 0.118 in
 ASTM D495
Comparative Tracking Index 600 V

@Thickness 3.00 mm
 600 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.710 mm
 7.0 - 14 sec

@Thickness 0.0280 in
 UL 746
15 - 29 sec

@Thickness 1.50 mm
 15 - 29 sec

@Thickness 0.0591 in
 UL 746
15 - 29 sec

@Thickness 3.00 mm
 15 - 29 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.710 mm
 >= 120 arcs

@Thickness 0.0280 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Middle Barrel Temperature 270 - 285 °C
518 - 545 °F
Front Barrel Temperature 280 - 290 °C
536 - 554 °F
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Melt Temperature 285 - 300 °C
545 - 572 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature <= 70.0 °C
<= 158 °F
Dry Time 1.00 - 3.00 hour
1.00 - 3.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 50 %