- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 446 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 446 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose Feature: Injection Molding, PA6+MF20%, General PurposeApplication: E&E (Rice Cooker Housing)Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DIN 53461; ASTM D648 |
| Kolon KOPA® KN333MS Low Friction Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| Lanxess Pocan® T 3150 XF 000000 PBT + PET, 55% Glass Fiber PBT+PET, 55% glass fibers, injection molding, improved flowability, low tendency to warp, increased temperature peak load, increased strength and increased modulus |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PET-G15 15% Glass Fiber Reinforced PET Features:High strengthGood heat resistanceApplications:Injection moldingApplication partsAuto partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75 |
| Solvay TECHNYL® A 52 G1 MX 20 PA66, Eh 0 Description: TECHNYL A 52 G1 MX20 is a Polyamide 6.6 glow wire resistant, reinforced with mineral fillerColors: it is marketed in black color.Available in: Latin AmericaMain Properties: ?Glow wire r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 3.20 mm |
446 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 LNP* STAT-LOY* 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 3.20 mm |
446 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 (Asia Pacific) LNP* Stat-loy* 9X03508 is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant, High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics LNP Thermocomp RB003 PA 66 (Europe-Africa-Middle East) 15% glass beads filled polyamide 66 injection moulding resinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® T-662 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® TY-181GC Nylon/Elastomer GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Toyobo T-661 Nylon 66, Standard Grade (DAM) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Cheng Yu Plastic N6G20 Nylon 6, 20% Glass Filled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Cheng Yu Plastic NGCV2 Flame Retardant Nylon 6, 20% Mineral Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| DSM Akulon® S223-D Nylon 66 (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| DSM Akulon® S223-DH Nylon 66 (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | DAM; ASTM D648 |
| DuPont Performance Polymers Zytel® FR7025V0F NC010 Nylon 66
(Unverified Data**) Zytel® FR7025V0F NC010 is a flame retardant polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.Information provided by DuPont Performance.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Eurostar Staramide A40 PA66, Extrusion Staramide A40 is Unreinforced, High Viscosity Polyamide 66, Extrusion ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| E-Polymers TEKAMID® TA210HS , Heat Stabilized PA66, DAM Heat stabilizedInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/B |
| Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Dry; ASTM D648 |
| Asahi Kasei Leona® 1502 Nylon 66 Similar to 1500 but with improved heat aging resistance.Applications:Under-the-hood automotive parts Information provided by Asahi Kasei |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Dry; ASTM D648 |
| Asahi Kasei Leona® 1700S Nylon 66 Similar to 1500 but with even higher molecular weight. Suitable for extrusion of thick-wall parts.Applications:Rods, films Information provided by Asahi Kasei |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 656 Nylon 6/6, Carbon/Glass Fiber Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/B |
| Ascend Performance Materials Vydyne® 20NSP BLK Nylon 66, DAM Vydyne® 20NSP BLK is a general-purpose, high nucleated, lubricated PA66 resin. Available in black, it is designed to crystallize rapidly in order to reduce cycle times and increase productivity thr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-2/B |
| Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||