Polymer Property : CTE, linear, Transverse to Flow = 5.56 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 10.0 - 110 µm/m-°C | 5.56 - 61.1 µin/in-°F | Average value: 66.2 µm/m-°C Grade Count:21 |
|
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl..
|
|||
| CTE, linear, Transverse to Flow | 10.0 - 85.0 µm/m-°C | 5.56 - 47.2 µin/in-°F | Average value: 64.0 µm/m-°C Grade Count:5 |
|
Overview of materials for Nylon 66, Unreinforced, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Temperature -30.0 - 30.0 °C
|
5.56
µin/in-°F <br>@Temperature -22.0 - 86.0 °F
|
ASTM D 696 |
|
SABIC Innovative Plastics LNP Thermocomp AF0029 ABS
LNP* Thermocomp* AF0029 is an ABS base resin containing Glass Fiber. Characteristics of this grade are Flame Retardancy.This data was supplied by SABIC-IP for the Americas region.
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Temperature -30.0 - 30.0 °C
|
5.56
µin/in-°F <br>@Temperature -22.0 - 86.0 °F
|
ASTM D696 |
|
SABIC Innovative Plastics LNP THERMOCOMP WF002 PBT
LNP* THERMOCOMP* WF002 is a compound based on PBT containing 10% Glass Fiber.
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Temperature 55.0 - 160 °C
|
5.56
µin/in-°F <br>@Temperature 131 - 320 °F
|
DAM; ISO 11359-1/-2 |
|
DuPont Performance Polymers Zytel® HTN FR52G30BL BK337 Polyphthalamide (PPA)
(Unverified Data**)
30% Glass Reinforced Flame Retardant PPA High Performance Polyamide Zytel HTNFR52G30BL BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin that has been devel..
|
|||
| CTE, linear, Transverse to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | DAM; ISO 11359-1/-2 |
|
DuPont Performance Polymers Zytel® PLS 93G35DH1 BK261 Nylon 6
(Unverified Data**)
35% Glass Reinforced Heat Stabilized Polyamide 6 Zytel PLS93G35DH1 BK261 is a 35% glass reinforced PA6 using SHIELD Technology only from DuPont it provides exceptional welding resistanceInformation ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 20NSP Nylon 66, DAM
Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 21SPC1 Nylon 66, DAM
Vydyne® 21SPC1 is a general-purpose, improved-flow, lubricated PA66 resin available in natural color. 21SPC1 offers a balanced combination of properties characterized by high strength, rigidity, go..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 21SPF BLK Nylon 66, Conditioned
Vydyne® 21SPF BLK is a, general-purpose PA66 resin used for extrusion-compounding. Available in black, it is designed principally for injection-molding fabrication. This grade offers a well-balance..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, DAM
Vydyne® 21SPF is general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grade offers a well-balanced combination of engineering propert..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359 |
|
Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded
Vydyne® 66B and 66J are members of a family of unreinforced extrusion grade Nylon 66 resins. They are available in natural color. These resins offer high strength, rigidity, and toughness for a bro..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 909 BK Nylon 66/6, 25% Glass Reinforced, DAM
Vydyne® 909 BK is a halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwrite..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R540H Nylon 66, 40% Glass Reinforced, DAM
Vydyne® R540H is general-purpose, heat-stabilized, hydrolysis-resistant, 40% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physic..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials VYDYNE® R543 Nylon, 43% Glass Reinforced, DAM
Vydyne® R543 is general purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine fee, flow and mold release. Glass..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, DAM
Vydyne® R543H BK02 is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in black, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R543H Black Nylon 66, 43% Glass Reinforced, DAM
Vydyne® R543H Black is general-purpose, hydrolysis-resistant, 43% glass-fiber reinforced PA66 resin. Available in black, it is an injection-molding grade resin that is lubricated for machine feed, ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R543H NT Nylon 66, 43% Glass Reinforced, DAM
Vydyne® R543H NT is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R543H Nylon 66, 43% Glass Filled, Dry as Molded
Vydyne® R543H is general-purpose, 43% glass-reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for improved machine feed, flow and mold release. ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R550 Nylon 66, 50% Glass Reinforced, DAM
Vydyne® R550 is general-purpose, hydrolysis-resistant, 50% glass-fiber reinforced PA66 resin. Available in natural, it is also lubricated for improved flow and offers superior surface appearance. G..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R550H Nylon 66, 50% Glass Reinforced, DAM
Vydyne® R550H is general-purpose, heat-stabilized, hydrolysis-resistant, 50% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physic..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, DAM
Vydyne® 65A is a medium-viscosity, heat-stabilized PA66 resin suitable for injection-molding extrusion and compounding applications. It is available in natural color only. Vydyne 65A resin offers h..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 66B Nylon 66, General Purpose, high viscosity, DAM
Vydyne® 66B is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66B resin offers high strength, ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 66R Nylon 66, General Purpose, high viscosity, DAM
Vydyne® 66R is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66R resin offers high strength, ..
|
|||
| CTE, linear, Transverse to Flow | 10.0 - 80.0 µm/m-°C | 5.56 - 44.4 µin/in-°F | Average value: 33.3 µm/m-°C Grade Count:3 |
|
Overview of materials for Nylon 66, Nucleated
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 20NSP BLK Nylon 66, DAM
Vydyne® 20NSP BLK is a general-purpose, high nucleated, lubricated PA66 resin. Available in black, it is designed to crystallize rapidly in order to reduce cycle times and increase productivity thr..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 66Z Nylon 66, DAM
Vydyne® 66Z is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66Z resin offers high strength, rigidity and toug..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded
Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® R633H Nylon 66/6, 33% Glass Reinforced, DAM
Vydyne® R633H is 33% glass-fiber reinforced PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, DAM
Vydyne® 21SPF1 is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding applications with the added benefits of improved flow during the molding ..
|
|||
| CTE, linear, Transverse to Flow |
10.0
µm/m-°C <br>@Thickness 2.00 mm,<br> Temperature 23.0 - 55.0 °C
|
5.56
µin/in-°F <br>@Thickness 0.0787 in,<br> Temperature 73.4 - 131 °F
|
ISO 11359-2 |
|
Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, DAM
Vydyne® M344 is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwri..
|
|||