- Polymer Property : Tensile Strength at Break = 75.0 MPa
Polymer Property : Tensile Strength at Break = 75.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | STN EN ISO 527-2 |
| Plastcom PLASTAMID® 6 BT B 27 PA6 Basic type PA 6 for compounding, for general use. Grade can contain PA 66 up to 5% and TiO2 content up to 0.25 %. Use: automotive, engineering, electrical and consumer-goods industryInformation Prov.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | STN EN ISO 527-2 |
| Plastcom PLASTAMID® 6 BT N 26 B/IM PA6 Basic type PA 6 for injection molding, for general use. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, hobby tools. Delivered in the natu.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® 104 PC UL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will.. |
|||
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Polykemi AB SCANAMID 66 A12^ X30 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | >= 75.0 MPa | >= 10900 psi | 50 mm/min; ISO 527-1,2 |
| Qualchem Danamid AFGFS2HUV30 Polyamide 66, 30% Glass Fiber Reinforced with glass fiber. Impact modified, heat and UV stabilized, for long-lasting use at 120-140°C, resistant to artificial lights.Information provided by Qualchem Zrt. |
|||
| Tensile Strength at Break | 75.0 - 100 MPa @Temperature 23.0 °C |
10900 - 14500 psi @Temperature 73.4 °F |
ISO 527-2/5 |
| PolyOne Bergadur™ PB400 G30 UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HPS6 PC (Europe-Africa-Middle East) Med/low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam e-beam and gamma sterilizable. .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| DSM Akulon® K223-HMS6 Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Grupo Repol Dinalon® A1S25 H PA66 Heat Stabilized Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 50H1 PA66, DRY Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phospho.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Solvay TECHNYL® B 218 Black 21 N PA66/6, DRY Description: Unreinforced copolyamide PA 66/6 , heat stabilized , medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® B 218 offers all of the primary proper.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM 1285 PEI (Europe-Africa-Middle East) Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM CRS5011R PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. Resin is RoHS compliant. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® 701 PBT (Asia Pacific) 35% glass/mineral alloy, excellent electrical performance to dielectric breakdown. Developed for automotive distributor caps.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® ENH8530 PBT+PET (Europe-Africa-Middle East) Non-Brominated & Non-Chlorinated Flame Retardant, 15% Glass fiber reinforced PBT/PET blend |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50mm/min; ISO 527 |
| Teijin Panlite® GN-3410R Improved Mold Release, Glass Fiber Reinforced, Flame Resistant Polycarbonate Resin GF 10% reinforced, flame retardant and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machin.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific) Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ASTM D638 |
| Unitika C300VN Characteristics: Flame resistant, transparent (flame resistance: UL94 V0, 0.8 mm) High flowInformation provided by Unitika Ltd. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-93 |
| Wellman Wellamid® 42L-XE-N Nylon 6, Engineering Grade All information provided by Wellman Engineered Resins. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-1,-2 |
| Covestro Makrolon® FR 7067 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BG-15/2 PA6-GF15 Product description: Grilon BG-15/2 is a heat stabilized PA6 injection molding grade with 15% glass fibers. Grilon BG-15/2 has the following important properties: Good surface finishEasy processingG.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® TSK-30/4 PA666-GB30 Product description: Grilon TSK-30/4 is a heat stabilized, normal viscosity PA66 +PA6 injection molding grade with 30% glass beads. Grilon TSK-30/4 has the following important properties: Good surfa.. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 80.0 °C |
10900 psi @Temperature 176 °F |
ASTM Test |
| BASF Petra® 130 FR BK-112 30% Glass Filled PET Petra 130 FR BK-112 is a 30% glass fiber reinforced, black pigmented, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene erephthalate feedstoc.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Conditioned (2.5% Moisture) Vydyne® R513H is general-purpose, 13% glass-reinforced, heat stabilized PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow, and mold .. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec |
10900 psi @Temperature 266 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® B3 GF 20 (2470) PA 6 Dry, 20% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 [mm/min]; ISO 527-1/2 |
| Akro-Plastic Akromid® S3 GF15 1 (3223) PA 6.10 Conditioned, 15% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 80.0 °C |
10900 psi @Temperature 176 °F |
50 mm/min, 1A; ISO 527 |
| SABIC Innovative Plastics SABIC STAMAX 40YM243 PP SABIC® STAMAX 40YM243 is a 40% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| LATI Latilub 88/50-20T PEEK, PTFE Filled Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Ter.. |
|||