Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.03 - 1.27 g/cc
0.0371 - 0.0459 lb/in³
Average value: 1.13 g/cc Grade Count:79
Water Absorption 0.490 - 10.5 %
0.490 - 10.5 %
Average value: 3.76 % Grade Count:55
Moisture Absorption at Equilibrium 0.250 - 5.00 %
0.250 - 5.00 %
Average value: 2.62 % Grade Count:43
Water Absorption at Saturation 4.50 - 9.00 %
4.50 - 9.00 %
Average value: 8.28 % Grade Count:19
Oxygen Transmission Rate 21.0 - 198 cc/m²/day
1.35 - 12.8 cc/100 in²/day
Average value: 51.2 cc/m²/day Grade Count:13
Nitrogen Transmission 7.80 cc-mm/m²-24hr-atm
19.8 cc-mil/100 in²-24hr-atm
Average value: 7.80 cc-mm/m²-24hr-atm Grade Count:10
Carbon Dioxide Transmission 113 cc-mm/m²-24hr-atm
287 cc-mil/100 in²-24hr-atm
Average value: 113 cc-mm/m²-24hr-atm Grade Count:10
Viscosity 3.30 - 51.0 cP
3.30 - 51.0 cP
Average value: 11.2 cP Grade Count:14
Viscosity Test 150 - 250 cm³/g
150 - 250 cm³/g
Average value: 203 cm³/g Grade Count:9
Maximum Moisture Content 0.00100 - 0.0800
0.00100 - 0.0800
Average value: 0.0668 Grade Count:12
Linear Mold Shrinkage 0.00300 - 0.0230 cm/cm
0.00300 - 0.0230 in/in
Average value: 0.0122 cm/cm Grade Count:38
Linear Mold Shrinkage, Transverse 0.00200 - 0.0180 cm/cm
0.00200 - 0.0180 in/in
Average value: 0.0113 cm/cm Grade Count:15
Melt Flow 1.20 - 162 g/10 min
1.20 - 162 g/10 min
Average value: 46.6 g/10 min Grade Count:15
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110 - 119
110 - 119
Average value: 116 Grade Count:11
Ball Indentation Hardness 90.0 - 170 MPa
13100 - 24700 psi
Average value: 121 MPa Grade Count:7
Tensile Strength, Ultimate 5.50 - 93.1 MPa
798 - 13500 psi
Average value: 61.8 MPa Grade Count:22
45.0 - 45.0 MPa

@Temperature 60.0 - 60.0 °C
6530 - 6530 psi

@Temperature 140 - 140 °F
Average value: 45.0 MPa Grade Count:1
Tensile Strength, Yield 25.0 - 90.0 MPa
3630 - 13100 psi
Average value: 63.5 MPa Grade Count:41
40.0 - 40.0 MPa

@Temperature 90.0 - 140 °C
5800 - 5800 psi

@Temperature 194 - 284 °F
Average value: 40.0 MPa Grade Count:1
40.0 - 40.0 MPa

@Time 1.80e+7 - 7.20e+7 sec
5800 - 5800 psi

@Time 5000 - 20000 hour
Average value: 40.0 MPa Grade Count:1
Film Elongation at Break, MD 510 - 540 %
510 - 540 %
Average value: 533 % Grade Count:4
Film Elongation at Break, TD 550 - 560 %
550 - 560 %
Average value: 555 % Grade Count:4
Elongation at Break 5.00 - 450 %
5.00 - 450 %
Average value: 96.6 % Grade Count:37
60.0 - 60.0 %

@Temperature 60.0 - 150 °C
60.0 - 60.0 %

@Temperature 140 - 302 °F
Average value: 90.0 % Grade Count:1
Elongation at Yield 3.00 - 150 %
3.00 - 150 %
Average value: 26.8 % Grade Count:26
Modulus of Elasticity 0.210 - 5.00 GPa
30.5 - 725 ksi
Average value: 2.55 GPa Grade Count:39
0.650 - 2.00 GPa

@Temperature 60.0 - 150 °C
94.3 - 290 ksi

@Temperature 140 - 302 °F
Average value: 1.15 GPa Grade Count:1
Flexural Yield Strength 7.00 - 140 MPa
1020 - 20300 psi
Average value: 74.9 MPa Grade Count:39
30.0 - 30.0 MPa

@Temperature 90.0 - 90.0 °C
4350 - 4350 psi

@Temperature 194 - 194 °F
Average value: 30.0 MPa Grade Count:1
Flexural Modulus 0.230 - 3.50 GPa
33.4 - 508 ksi
Average value: 2.23 GPa Grade Count:44
0.850 - 0.850 GPa

@Temperature 90.0 - 90.0 °C
123 - 123 ksi

@Temperature 194 - 194 °F
Average value: 0.850 GPa Grade Count:1
Poissons Ratio 0.400 - 0.410
0.400 - 0.410
Average value: 0.405 Grade Count:4
Secant Modulus, MD 0.190 - 0.210 GPa
27.6 - 30.5 ksi
Average value: 0.200 GPa Grade Count:4
Secant Modulus, TD 0.200 - 0.230 GPa
29.0 - 33.4 ksi
Average value: 0.208 GPa Grade Count:4
Izod Impact, Notched 0.267 - 7.47 J/cm
0.500 - 14.0 ft-lb/in
Average value: 2.11 J/cm Grade Count:18
1.0678 - 2.1356 J/cm

@Temperature -40.0 - -20.0 °C
2.0004 - 4.0009 ft-lb/in

@Temperature -40.0 - -4.00 °F
Average value: 1.51 J/cm Grade Count:2
1.0678 - 2.1356 J/cm

@Thickness 3.17 - 3.17 mm
2.0004 - 4.0009 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 1.51 J/cm Grade Count:2
Izod Impact, Notched (ISO) 3.00 kJ/m² - NB
1.43 ft-lb/in² - NB
Average value: 12.4 kJ/m² Grade Count:14
2.50 - 85.0 kJ/m²

@Temperature -30.0 - -30.0 °C
1.19 - 40.4 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 21.0 kJ/m² Grade Count:5
Charpy Impact Unnotched 4.50 J/cm² - NB
21.4 ft-lb/in² - NB
Average value: 8.27 J/cm² Grade Count:27
3.60 J/cm² - NB

@Temperature -40.0 - -20.0 °C
17.1 ft-lb/in² - NB

@Temperature -40.0 - -4.00 °F
Average value: 6.87 J/cm² Grade Count:13
Charpy Impact, Notched 0.300 J/cm² - NB
1.43 ft-lb/in² - NB
Average value: 1.01 J/cm² Grade Count:25
0.250 J/cm² - NB

@Temperature -40.0 - -20.0 °C
1.19 ft-lb/in² - NB

@Temperature -40.0 - -4.00 °F
Average value: 1.31 J/cm² Grade Count:13
Coefficient of Friction 0.210 - 0.510
0.210 - 0.510
Average value: 0.357 Grade Count:6
Coefficient of Friction, Static 0.280 - 0.940
0.280 - 0.940
Average value: 0.507 Grade Count:4
Film Tensile Strength at Break, MD 40.0 - 42.0 MPa
5800 - 6090 psi
Average value: 41.0 MPa Grade Count:4
Film Tensile Strength at Break, TD 39.0 - 43.0 MPa
5660 - 6240 psi
Average value: 40.5 MPa Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+9 - 1.00e+15 ohm-cm
1.00e+9 - 1.00e+15 ohm-cm
Average value: 4.88e+14 ohm-cm Grade Count:28
Surface Resistance 1.00e+10 - 1.00e+15 ohm
1.00e+10 - 1.00e+15 ohm
Average value: 2.41e+14 ohm Grade Count:12
Dielectric Constant 3.60 - 8.00
3.60 - 8.00
Average value: 4.47 Grade Count:8
Dielectric Strength 13.0 - 120 kV/mm
330 - 3050 kV/in
Average value: 25.5 kV/mm Grade Count:20
Dissipation Factor 0.0200 - 0.300
0.0200 - 0.300
Average value: 0.0580 Grade Count:9
Comparative Tracking Index 400 - 600 V
400 - 600 V
Average value: 590 V Grade Count:22
Hot Wire Ignition, HWI 7.00 - 120 sec
7.00 - 120 sec
Average value: 40.8 sec Grade Count:4
High Amp Arc Ignition, HAI 120 arcs
120 arcs
Average value: 120 arcs Grade Count:4
High Voltage Arc-Tracking Rate, HVTR 10.1 - 25.4 mm/min
0.398 - 1.00 in/min
Average value: 17.8 mm/min Grade Count:3