Polymer Property : Film Tensile Strength at Break, TD = 39.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ASTM D882
NOVA Chemicals Sclair® 14G Butene LMDPE Film Resin Film Properties. Features: Low gel, good opacity, easy processability.Applications: Overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ASTM D882
NOVA Chemicals Sclair® 15A Butene HDPE Film Resin Film Properties. Features: Low gel, good barrier properties, strength and toughness.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ASTM D882
Eastman 9921 PET Film (discontinued **) VORIDIAN polymer 9921 is a copolymer PET that has been crystallized. Color concentrates of polymer 9921 are available on request.Applications/UsesAutomotive parts containersFood packagingHousehold p..
Film Tensile Strength at Break, TD	39.0 - 43.0 MPa	5660 - 6240 psi	Average value: 40.5 MPa Grade Count:4
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb ..
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ASTM D882-02
Ipiranga Petrochem LBH 0120 BP LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi
UBE 5034FDX17 Air Blown Nylon 6/66 Film Specialties: Special grade for Air blownLow curlHigh transparencyHigh shrinkGood thermoform-abilityApplications: Best for Air BlownProcessing: Pouch (Air blown)Information provided by UBE.
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	50 µm (2 mil) film; ASTM D882
DuPont Elvax® 3165 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film 18 wt% Vinyl Acetate.Elvax® 3165 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins..
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ISO 527-3
Total EVA 1005 VN 5 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1005 VN 5 is made by a high pressure tubular process. Grade for films with high transparency and good mechanical properties. Contains an antioxidant.Application examples: Coextrusion, stretch ..
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ISO 527-3
Dow INSPIRE™ 112 Performance Polymer INSPIRE™ 112 Performance Polymer is a propylene-based resin intended for use in film and sheet extrusion.Information provided by Dow
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ASTM D882
Eastman 9921W PET Film (discontinued **) Voridian PET 9921W is a copolymer PET. Typical applications include containers for automotive parts, household products, and pharmaceutical and food packaging. Voridian PET thermoplastic polyesters ..
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ASTM D882
NOVA Chemicals Sclair® 14J1 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, good clarity, high strength and toughness.Applications: Produce film.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	39.0 MPa	5660 psi	ISO 527-3
Borealis Borstar® FB4370 Medium Density Polyethylene Borstar® FB4370 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Applications: Borstar® FB4370 has been developed especially for ap..