Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.230 GPa | 33.4 ksi | ASTM D790 |
ExxonMobil Escorene® LD-421 LDPE Power Cable Insulation
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A crosslinkable polyethylene homopolymer designed as an electrical grade base resin.Applications: A base resin for fully formulated crosslinkable me.. |
|||
Flexural Modulus | 0.230 - 3.50 GPa | 33.4 - 508 ksi | Average value: 2.23 GPa Grade Count:44 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | cond., 2 mm/min; ISO 178-A |
Lanxess Durethan® BC 700 HTS DUSXBL 900116 Nylon 6, Impact Modified PA 6, non-reinforced, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | 1% secant at 0.05 in/min; ASTM D790A |
LyondellBasell Adflexâ„¢ KS-021P TPO Resin Primary Processing Method: Blown Film/Impact ModificationKey Features: excellent low temperature impact resistance, excellent chemical and environmental stress-cracking resistance, FDA acceptable, n.. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP YL003 Polyester Elastomer LNP* LUBRICOMP* YL003 is a compoudn based on Polyester Elastomer resin containing 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP YL003 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YL003 is a compound based on Polyester Elastomer containing PTFE. Added features include; Internally Lubricated. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | ASTM D790 |
Toyobo PELPRENE™ S2002FB Polyester TPE, Flame Resistant Features: Polyester TPE, Flame ResistantInformation provided by Toyobo. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | ISO 178 |
Chengdu Polyster FH605 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H605 and self-made flame retardant material. Flame retardant, high tear resistance. Applications requiring flame retardancy, such as wires, cables and optical fiber.Information provided by .. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | ASTM D790 |
DuPont™ Surlyn® 8660 Ionomer Resin, Sodium Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Flexural Modulus | 0.230 GPa | 33.4 ksi | Conditioned; ISO 178 |
Lanxess Durethan® BC 700 HTS 900116 Nylon 6/66
(discontinued **) PA 6/66 |