Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 30.0 - 40.0 MPa | 4350 - 5800 psi | Injection and Compression; ISO 527 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Tensile Strength, Yield | 1.38 - 40.0 MPa | 200 - 5800 psi | Average value: 14.8 MPa Grade Count:50 |
Overview of materials for Epoxy Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Adhesive". Each property range of values reported is minimum and maximum values of appropriate Mat.. |
|||
Tensile Strength, Yield | 0.130 - 40.0 MPa | 18.9 - 5800 psi | Average value: 18.4 MPa Grade Count:80 |
Overview of materials for High Density Polyethylene (HDPE), Ultra High Molecular Weight This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Ultra High Molecular Weight". Each property range of values reported i.. |
|||
Tensile Strength, Yield | 40.0 - 40.0 MPa @Temperature 90.0 - 140 °C |
5800 - 5800 psi @Temperature 194 - 284 °F |
Average value: 40.0 MPa Grade Count:1 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Tensile Strength, Yield | 40.0 - 40.0 MPa @Time 1.80e+7 - 7.20e+7 sec |
5800 - 5800 psi @Time 5000 - 20000 hour |
Average value: 40.0 MPa Grade Count:1 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Tensile Strength, Yield | 34.0 - 40.0 MPa @Thickness 2.00 mm |
4930 - 5800 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF) Solef® 60512 PVDF copolymer has high viscosity of the melt and it is a grade for offshore piping.Features: Copolymer; High ViscosityUses: PipingAdditional Properties: Crystallization Heat - ASTM .. |
|||
Tensile Strength, Yield | 30.0 - 40.0 MPa @Thickness 1.50 mm |
4350 - 5800 psi @Thickness 0.0591 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 60512/0550 and 60512/0150 Polyvinylidene Fluoride (PVDF) Solef® 60512/0550 and Solef® 60512/0150 are PVDF grades compounded with PTFE for extrusion of anti-wear tapes.Features: CopolymerUses: TapeAdditional Properties: Crystallization Heat - ASTM D3.. |
|||
Tensile Strength, Yield | 34.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
4930 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 60512 PVDF copolymer has high viscosity of the melt and it is a grade for offshore piping.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength, Yield | 21.0 - 40.0 MPa | 3050 - 5800 psi | Average value: 28.4 MPa Grade Count:9 |
Overview of materials for Polypropylene, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Wood Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
Tensile Strength, Yield | 0.110 - 40.0 MPa | 16.0 - 5800 psi | Average value: 12.9 MPa Grade Count:484 |
Overview of materials for Thermoset Polyurethane, Elastomer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Elastomer, Unreinforced". Each property range of values reported is minimum and .. |