Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Resources ABS-GP1 General Purpose ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources ABS-GP1 General Purpose ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General Purpose Acrylonitrile Butadiene StyreneFeatures: • Medium Impact ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 3.0 - 14 g/10 min

@Load 3.80 kg,
Temperature 230 °C
3.0 - 14 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength at Break 39.3 MPa
5700 psi
ASTM D638
Tensile Strength, Yield 42.1 MPa
6100 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ASTM D638
Tensile Modulus 2.62 GPa
380 ksi
ASTM D638
Flexural Strength 64.1 MPa
9300 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature -40.0 °C
1.00 ft-lb/in

@Temperature -40.0 °F
ASTM D256
2.14 J/cm

@Temperature 22.8 °C
4.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Izod Impact, Notched (ISO) 7.35 kJ/m²

@Temperature -30.0 °C
3.50 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
16.4 kJ/m²

@Temperature 22.8 °C
7.80 ft-lb/in²

@Temperature 73.0 °F
ISO 180/1A
Charpy Impact, Notched 1.89 J/cm²

@Temperature 22.8 °C
9.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 22.6 J
16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C
190 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C
180 °F
ASTM D648
Vicat Softening Point 98.9 °C
210 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 188 - 210 °C
370 - 410 °F
Middle Barrel Temperature 204 - 227 °C
400 - 440 °F
Front Barrel Temperature 216 - 238 °C
420 - 460 °F
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 48.9 - 71.1 °C
120 - 160 °F
Drying Temperature 82.2 - 93.3 °C
180 - 200 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001