- Polymer Property : Melt Flow = 3.0 g/10 min
Polymer Property : Melt Flow = 3.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| PolyOne Maxxam™ DP 4980-1-1000 Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Plastcom SLOVAMID 6 GF 15 Polyamide 6, 15% Glass Fiber FeaturesPA 6 for injection moulding, chemically reinforced with 15% glass fiber. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and .. |
|||
| Melt Flow | 3.0 g/10 min @Load 0.325 kg, Temperature 270 °C |
3.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVAMID 66 GF 50 LS PA66, 50% glass fibre, light stability FeaturesChemically reinforced with 50% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry, l.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Plastcom SLOVAMID 66 T 30 Polyamide 66, 30% Mineral Filled FeaturesPA 66 with the content of 30% chemically modified mineral filler. Used for holders of electric hand tools, hobby tools, gears, covers of electric tools, flat products, automobile wheel cove.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 275 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 527 °F |
STN EN ISO 1133 |
| Plastcom SLOVAMID® 6/6T GF 35 TS PA6/6T reinforced with glass fiber, improved heat resistance PA 6/6T for injection molding, reinforced with 35% of glass fiber, for moldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry, improved.. |
|||
| Melt Flow | 3.0 - 18 g/10 min @Load 6.70 kg, Temperature 337 °C |
3.0 - 18 g/10 min @Load 14.8 lb, Temperature 639 °F |
ASTM D1238 |
| Polymer Resources PEI-G40 Polyetherimide, 40% Glass Reinforced Polyetherimide, 40% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly.. |
|||
| Melt Flow | 3.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 - 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized Information provided by Ravago. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Solvay Specialty Polymers KetaSpire® KT-820 NL Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire PEEK is produced to the highest industry standard.. |
|||
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D-1238 |
| Chevron Phillips EB6025 HIPS - High Impact Polystyrene
(discontinued **) Rubber modified high impact polystyrene.Applications:Cosmetic packagingShower surroundsPoint of purchase displaysThin-wall injection molding and thermoformingFeatures:Smooth, glossy surface finishGo.. |
|||
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Ineos Nova 271 High Performance Styrenic Enhanced Polystyrene
(discontinued **) Excellent balance of stiffness, heat resistance, and impact properties, Custom colorsApplications: Injection molding and extrusion, Applications requiring strength and durability where custom colori.. |
|||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ExxonMobil Method |
| ExxonMobil LD 145.PX Packaging Resin
(discontinued **) LD 145.PX resin is a homopolymer cast film resin offering good clarity and toughness. Applications include Bread bags and other Food Packaging.Information provided by ExxonMobil Chemical |
|||
| Melt Flow | 3.0 g/10 min @Load 12.5 kg, Temperature 200 °C |
3.0 g/10 min @Load 27.6 lb, Temperature 392 °F |
2 mm x 8 mm |
| Ineos Barex® 218 E Acrylonitrile-Methyl Acrylate Copolymer Extrusion Grade. Barex® Resins are available in either natural or blue tint. Barex® 218E is most commonly used for thermoformed sheet applications in which high impact performance is require.. |
|||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Lucent Polymers PC-1403 Polycarbonate, Extrusion/Blow Molding Grade Medium FlowAdd "R" for Added ReleaseAdd "U" for UVÂ StabilizedInformation provided by Lucent Polymers, Inc. |
|||
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| MRC Polymers NAXALOYâ„¢ 770 ABS + PC Alloy Impact modifiedAvailable in Natural, Black, and GrayCan be Colored (Masterbatch)Low temperature ductility and impact modifiedCan be UV StabilizedInternal and external lubricant can be addedInformati.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Solvay Specialty Polymers KetaSpire® KT-XXXX Polyetheretherketone (PEEK) KetaSpire® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire® PEEK is produced to the highest industry standards and is cha.. |
|||
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM Data |
| Styron CALIBRE™ 603 3 Polycarbonate, Branched CALIBRE® 603 is a branched polycarbonate resin and is equipped with a mold release and a UV stabilization package. CALIBRE 603 resins exhibit an excellent property balance of high clarity, high m.. |
|||
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Styron Pulse® 930 ABS + Polycarbonate PULSE® 930 Engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at room temperature. PULSE 930 Engineering resin has been used i.. |
|||
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Sumitomo Chemical Sumipex® BF3 Acrylic Resin, GP Blow Molding Grade Product CharacteristicsExcellent WeatherabilityHigh TransparencyGood Heat ResistanceInformation provided by Calsak Corporation |
|||
| Melt Flow | 3.0 g/10 min @Load 10.0 kg, Temperature 200 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 392 °F |
ASTM D1238 |
| Supreme Petrochem SP 6460 High Heat Polystyrene Characteristics High impact and modulus Easy flow High heat resistance & strength Available in any dark colorProcessing Injection moldingApplications Instrument enclosures Automobile interior pa.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 10306 is a brown color concentrate based in linear low density polyethylene. This product was formulated to offer color and opacity in polyethylene film applications. POLYBA.. |
|||
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133H |
| Total PS CPDS FT876 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) FT876 is a high impact, halogen free flame retardant polystyrene with good thermal stability and processability.Main Characteristics:Bromine and Chlorine free,UL94 V.. |
|||
| Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
| Melt Flow | 3.0 g/10 min @Temperature 230 °C |
3.0 g/10 min @Temperature 446 °F |
I<sub>2</sub>; ASTM D1238 |
| Formosa Plastics Formolene® 5143S Homopolymer Polypropylene Homopolymer for Extrusion Sheet and Thermoforming Applications Formolene® 5143S is a higher melt flow homopolymer designed for light weighting of components. Its very high stiffness enables reducti.. |
|||
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Covestro Makrolon® 1143 Polycarbonate Pseudoplastic behavior and high viscosity extrusion grade with UV stabilizer and easy mold release, special grade for twin-wall sheet.Information provided by Bayer.As of 1 September 2015, Bayer Mate.. |
|||
| Melt Flow | 3.0 - 57 g/10 min | 3.0 - 57 g/10 min | ASTM D1238 |
| Buckeye Polymers BP FLEX A6310 BLK Thermoplastic Elastomer SEBS Product Information: BP Flex Thermoplastic Elastomers are based on SEBS polymers (Styrene-ethylene/butylene-styrene) providing increased oxidation and weather resistance, higher service temperatures.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Arkema Group Orgalloy® RS 6030 Polyamide 6 Alloy 30% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
| Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Dry) Designation ISO 1874-PA12,M,16-120,CF30Rigid grade with carbon fiber filler (30%) for injection molding. Available color: black.Very high rigidity. High strength-to-weight ratio. Very low shrinkage:.. |
|||
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
|
| Ineos ABS TRIAX® 1408 GF ABS/Nylon Blend, Injection Grade, Dry as Molded
(discontinued **) Injection molding grade, higher stiffness, good stress corrosion cracking resistance and chemical resistance (fuel, cleaning agents).Information provided by Bayer.LANXESS was spun-off from Bayer in .. |
|||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| ExxonMobil Escorene™ FL 00328 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00328 is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions: Processing temperatures above 220°C (428°F) may cause resin degradation. Machine.. |
|||