Polymer Resources ABS-G25 ABS, 25% Glass Reinforced

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources ABS-G25 ABS, 25% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Acrylonitrile Butadiene Styrene, 25% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Melt Flow 0.50 - 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
0.50 - 5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 93.1 MPa
13500 psi
ASTM D638
Tensile Strength, Yield 93.1 MPa
13500 psi
ASTM D638
Elongation at Yield 1.5 %
1.5 %
ASTM D638
Flexural Strength 128 MPa
18500 psi
ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
1.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
220 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 191 - 199 °C
375 - 390 °F
Middle Barrel Temperature 210 - 221 °C
410 - 430 °F
Front Barrel Temperature 210 - 227 °C
410 - 440 °F
Melt Temperature 210 - 238 °C
410 - 460 °F
Mold Temperature 48.9 - 60.0 °C
120 - 140 °F
Drying Temperature 79.4 - 85.0 °C
175 - 185 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001