Polymer Property : Linear Mold Shrinkage = 0.0010 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Nylene® Norpex® AX30GF , 30% Glass Reinforced Polyphenylene Ether
Description: Norpex® AX30GF is a 30% glass fiber reinforced Polyphenylene Ether. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric..
Linear Mold Shrinkage 0.0010 - 0.0025 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0025 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 4000 AFA-6145 V0 (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber - Flame Retardant
Linear Mold Shrinkage 0.0010 - 0.0025 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0025 in/in

@Thickness 0.125 in
ASTM D 955
RTP Company RTP 4099 X 123510 A Polyphthalamide (PPA), Carbon Fiber - Aramid Fiber - Impact Modified - PTFE Lubricated - Silicone Lubricated
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0020 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 709 High Density Polyethylene (HDPE), Glass Fiber
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D 955
RTP Company RTP PP 30 GF FR0 NAT Polypropylene (PP), Glass Fiber - Flame Retardant - Value Product - UL94
Flame Retardant - Glass Fiber - Value Product
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
Injection; ISO 2577
Raschig Group SURAPLAST UPA 63 UP
Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
PolyOne Edgetek® LC-30GF/000 LCP (Liquid Crystal Polymer), 30% Glass Reinforced, Hi-Temp  (discontinued **)<
Information provided by PolyOne™ Corporation
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
Lehmann & Voss LUVOCOM® 50-1396 Polycarbonate, with carbon fiber, glass fiber and PTFE, electrically conducting
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi..
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
IDI Composites A-205 Thermoset Polyester, Sheet
AUTOMOTIVE - Versatile family of compounds specifically designed for automotive structural applications. Low shrink characteristics, heat resistance, long-term dimensional stability, and corrosion r..
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
LG Chemical LUPOS HR-2307 Heat Resistant SAN, 30% Glass Fiber Reinforced
LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have ..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
0.125; ASTM D955
LTL Color Compounds ColorFast® PCGF120 Polycarbonate, 20% Glass-Filled
20% glass-filled grade, good balance of impact and mechanical propertiesAll information provided by LTL Color Compounders, Inc.
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
Lehmann & Voss LUVOCOM® 1105/XCF/15-S PEEK, with carbon fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at..
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Techmer ES Electrafil® M-2386 NAT Polycarbonate
Linear Mold Shrinkage 0.0010 - 0.0060 cm/cm

@Thickness 3.20 mm,
Time 259000 sec
0.0010 - 0.0060 in/in

@Thickness 0.126 in,
Time 72.0 hour
ISO 294
A. Schulman FORMION™ FI 231 5% Mineral Reinforced Ionomer / Nylon Alloy
DescriptionFormion® FI 231 is an injection molding grade, 5% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness. Ap..
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Copolymer Polypropylene
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0040 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 105 CC HI Polypropylene (PP), High Impact - Glass Fiber - Chemically Coupled
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 1305 Polyphenylene Sulfide (PPS), Glass Fiber - UL94 V-0
This series of compounds offer outstanding strengths combined with good heat and chemical resistance which may successfully be maintained in low load applications operating up to 500F. These igniti..
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0040 in/in

@Thickness 0.125 in
ASTM D 955
RTP Company RTP 182 HEC Polypropylene (PP), Nickel-Coated Carbon Fiber - EMI/RFI Shielding - Electrically Conductive
Linear Mold Shrinkage 0.0010 - 0.0050 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0050 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 205 D TFE 20 Nylon 6/12 (PA), Glass Fiber - PTFE Lubricated
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
MD; ASTM D955
Aclo Accutech ABS ABS833G30L Glass Reinforced
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
MD; ASTM D955
Aclo Accutech Polycarbonate POL050G40L Glass Reinforced
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
Cold Part VS Cold Tool; ASTM D955
Applied Composites 8092 Polyester SMC
Industry Application: ConstructionProduct Application: Building ProductsDistinct Features: Pigmentable, High Molding Efficiency, Low Thermal ExpansionInformation provided by Applied Composites Corpo..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Bulk Molding Compounds BMC 1608 Very High Strength, Corrosion Resistant
BMC 1608 is a very high strength, general purpose, corrosion resistant material. Recommended for compression molding only. UL® recognized. Meets FDA requirements for food contact. This material was..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Cheng Yu Plastic A707G2 SAN, 20% Glass Fiber
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
PolyOne Edgetek® PE-25CF/000 High Density Polyethylene (HDPE), Carbon Fiber Reinforced  (discontinued **)
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Bulk Molding Compounds BMC T40(18)-LS Die Casting Replacement Grade Molding Compound
BMC T40(18)-LS is a low shrink compound designed as a direct replacement for aluminum die casting applications. T40(18)-LS is UL recognized. Excellent mechanical properties and dimensional stabili..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
ASTM D 955
RTP Company RTP 1399 X 106389 Polyphenylene Sulfide (PPS); Carbon Fiber Reinforced - Internally Lubricated - Wear Resistant
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 207 D Nylon 6/12 (PA), Glass Fiber
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Sumitomo Bakelite North America RX® 853G Fiberglass Reinforced Phenolic Novolac
RX® 853G is a fiberglass reinforced phenolic novolac compound, featuring dimensional stability, moderate impact resistance, and good strength and modulus.Information supplied by Sumitomo Bakelite N..
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Adell ER-39 Polypropylene Homopolymer; 43% Glass Reinforced, High Stiffness
Data provided by Adell Plastics, Inc.