Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.50 g/10 min @Load 0.325 kg, Temperature 270 °C |
0.50 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
Plastcom SLOVALEN PC 16 FRD 1 PP, flame retardant Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips 7105GLT LLDPE Blown Film Resin, Hexene Copolymer
(discontinued **) Resin Type: Hexene Copolymer, High Antiblock, High Slip, Processing Aid Version of 7105T, Cast/Blown Film ResinCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or .. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Condition E; ASTM D1238 |
Chevron Phillips Vytek™ V205C3 Enhanced LLDPE Blown Film Resin
(discontinued **) Resin Type: slip, antiblock, and processing aid additivesCharacteristics: excellent dart impact, hot-tack and heat seal properties, good drawdown, can be used straight or blendedApplications: thick .. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238E |
Chevron Phillips Dynex™ D605A6 Enhanced LLDPE Blown Film Resin
(discontinued **) Resin Type: enhanced linear low density polyethylene, high antiblock, and processing aid additiveCharacteristics: superior dart impact, optical, hot-tack and heat seal properties, good drawdown, can.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Condition E; ASTM D 1238 |
Eastman 5284 LDPE 8% EVA Copolymer, High Clarity, Ultra-High Impact Film Resin
(discontinued **) Resin Type: CopolymerCharacteristics: Excellent Heat Seal Characteristics, Superior Impact Strength, Good Optical Properties, No Slip, High Antiblock, High Coefficient of FrictionApplications:Ice Ba.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
Huntsman PE1501 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with excellent impact strength, good heat seal, and good clarity.Applications: Film extrusion: greenhouse film, heavy-duty packa.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® NA362176 Low Density Polyethylene ApplicationsPETROTHENE NA 362 is a series of low density/EVA copolymers designed for ice bags, bag-in-box, heavy-duty skin packaging and other high strength, easy to seal packaging. NA 362 exhibits.. |
|||
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Ineos HP54-60 Flake Polyethylene Copolymer Flake This is a high density polyethylene copolymer flake which contains no additives and is not pelletized. It is designed for use in the plastic wood composite market.Information provided by Ineos Olef.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® NA362005 Low Density Polyethylene ApplicationsPETROTHENE NA 362 is a series of low density/EVA copolymers designed for ice bags, bag-in-box, heavy-duty skin packaging and other high strength, easy to seal packaging. NA 362 exhibits.. |
|||
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LyondellBasell Astryn BA16G Polypropylene Copolymer Key Features: fractional melt flow, medium modulus, UV-stabilized, extrusion grade polypropylene copolymer, good flexibility, high impact strength, good colorability, good processability, good weath.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ISO 1133 |
Solvay Specialty Polymers Catalyst PS/2 Polyolefin Catalyst PS/2 is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that take place by exposure of the pipe to water or steam .. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ISO 1133 |
Solvay Specialty Polymers Catalyst PS/2LR Polyolefin Catalyst PS/2LR is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or .. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ISO 1133 |
Solvay Specialty Polymers Polidan® T/A-HF Polyethylene, Crosslinked (XLPE) POLIDAN® T/A-HF is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction. It is used for flexible crosslinkable pipes.Featu.. |
|||
Melt Flow | 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Teknor Apex MONPRENE® MP 2835E Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ PP 3045 Information provided by A. Schulman. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
UBE R500 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Westlake EBAC® SP1802 22.5% Ethylene Butyl Acrylate Copolymer Westlake EBAC® SP1802 is a 22.5% EBA copolymer designed for blown film, tie-layer, coextrusions and blending where flexibility and strength are important. SP1802 provides excellent elasticity and l.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
Westlake Hifor Xtreme SC74844 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74844 polymer is a high strength linear low density polyethylene designed for blown film extrusion that contains medium slip, high antiblock and processing aid. Films produce.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
Westlake Hifor Xtreme SC74858 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74858 polymer is a high strength, good clarity linear low density polyethylene designed for blown film extrusion that contains no slip or antiblock and processing aid. Films .. |
|||
Melt Flow | 0.50 g/10 min @Temperature 230 °C |
0.50 g/10 min @Temperature 446 °F |
I<sub>2</sub>; ASTM D1238 |
Formosa Plastics Formolene® 6600A Impact Copolymer Polypropylene Impact Copolymer for Extrusion and Compounding Applications (Fractional Melt Flow) Formolene® 6600A is a high impact copolymer with an excellent balance of toughness and stiffness. It is suitable f.. |
|||
Melt Flow | 0.50 - 1.5 g/10 min @Temperature 230 °C |
0.50 - 1.5 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ PP 3045 Information provided by A. Schulman. |
|||
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Enable™ 27-05HH Metallocene Polyethylene Resin Product Description: Enable 27-05HH is a metallocene ethylene-hexane copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact and .. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
ExxonMobil LDPE LD 361BW Low Density Polyethylene Resin Product Description: LD 361 series are LEVA LDPE grades, offering good mechanical and sealing properties. Several additive combinations are available according to the required surface properties.Ava.. |
|||
Melt Flow | 0.50 - 30 g/10 min | 0.50 - 30 g/10 min | I2; ASTM D1238 |
Dow Engage® Polyolefin Elastomer Engage® thermoplastic elastomers are ethylene octene copolymers produced via advanced INSITE™ catalyst and process technology, allowing control over polymer structure, properties, and rheology. .. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
Dow FLEXOMER™ ETS-9066 NT 7, 0.8 mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9066 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an.. |
|||
Melt Flow | <= 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C |
<= 0.50 g/10 min @Load 11.0 lb, Temperature 392 °F |
|
Chi Mei Kibiton® PB-5301 SBC Asphalt modifier |
|||
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
E-Polymers EFLEX® S5050 Extrusion S-series ( SBS, SEBS compound resins): E-FLEX S series resins are based on SBS/SEBS/SEEPS/PP exhibiting excellent high and low temperature resistance and easy processing with conventional thermoplas.. |
|||
Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Condition E; ASTM D1238 |
Chevron Phillips Dynex™ D605C3 Enhanced LLDPE Blown Film Resin
(discontinued **) Resin Type: enhanced linear low density polyethylene, slip, antiblock and processing aid additivesCharacteristics: superior dart impact, optical, hot-tack and heat seal properties, good drawdown, ca.. |
|||
Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238/E |
Borealis Borstar® HE6063 Natural Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar HE6063 is a natural, colorable, bimodal, high-density polyethylene compound, produced using the Borstar process, for jacketing of power and telecommunications cables. It is characterized by.. |