- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 104 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 104 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Quadrant EPP Acetron® POM-C Copolymer Acetal, Porosity-Free, Unfilled, Extruded |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Polymer Resources AC-GP2-TFE5 Acetal Copolymer, 5% PTFE Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| Shell Carilon® DP R1000 Polyketone
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1000 is a high flow developmental engineering polyketone resin from Shell Chemi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 - 263 °C | 219 - 505 °F | Average value: 225 °C Grade Count:53 |
| Overview of materials for Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber". Each property range of values reported is mi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D 648 |
| RTP Company RTP 800 TFE 15 SI 2 Z Acetal (POM), PTFE & Silicone Lubricated - FDA Compliant Ingredients |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | Unannealed, 0.125 in bars; ASTM D648 |
| PolyOne Lubri-Tech™ AT-000/8T Acetal-Copolymer, PTFE Lubricated
(discontinued **) Description/Features:PTFE LubricatedInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP COLORCOMP DX06407H PC LNP* COLORCOMP* DX06407H is an unfilled Polycarbonate. Added features of this material include: Easy Molding, Mold Release, Healthcare |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| RTP Company RTP 200D MS Nylon 6/12 (PA 6/12) Molybdenum Disulfide
(discontinued **) Molybdenum DisulfideComments:Molybdenum DisulfideUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Com.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Annealed, 80°C, 4 hours; ISO 175 |
| LG Chemical XR-472 ABS, High Heat Resistance, High Gloss Information Provided by LG Chem |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® PAHF Polycarbonate-ABS Alloy General purpose HB-rated PC/ABS with improved chemical resistanceAll information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP (Asia Pacific) LNP* LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing PTFE, Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® ABS CF5 5% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 5% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics XYLEX X7507 PC+POLYESTER (Europe-Africa-Middle East) F-1 weathering certified in natural color, specially designed for Pool & Spa applications. Currently available in natural color only. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Europe-Africa-Middle East) PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP DX07350 PC (Asia Pacific) Lexan *DX07350 resin is a glass filled, Non-brominated & Non-chlorinated flame retardant polycarbonate. High stiffness and good flow. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Techmer ES Plaslube® AC-81/TF/15 NAT Acetal (POM) Homopolymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| Samyang Triloy® 120H PC/ABS alloy Characteristics:Impact resistantChemical resistantDimensional stabilityProcessabilityGood flowApplications:Automotive bumperAutomotive outdoor handleAll information provided by Samyang |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.17 mm |
220 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® A230G ABS Molding Resin, 30% Glass Fiber Reinforced Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ISO 75-2 |
| Denka MALECCA K-400 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Ensinger TECATRON™ PPS Polyphenylene sulfide (PPS) TECATRON PPS is a high performance thermoplastic that combines good mechanical properties with excellent thermal and chemical resistance properties. There is no known solvent that dissolves TECATRON.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Asahi Kasei Thermylene® P-05FG-0870 5% Glass Reinforced, UV Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ISO 75-1, -2 |
| C 9021 XAP2 LS POM, UV Resistant POM copolymerInformation provided by Celanese |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 243 SAN, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron HR-105 ABS Super Heat Resistant High Heat Resistant Grades with Better Flow characteristicInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| 203 PPS, Unfilled A very easy flowing unfilled grade. This grade demonstrates excellent chemical resistance and thermal stability. Intended for extrusion applications that do not require high melt strength and for c.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| 317 PPS, Unfilled 0317 exhibits a high melt strength for extrusion processes. The material demonstrates excellent heat and chemical resistance. The intended use of this product is for extruding monofilament/fibers, r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D 648 |
| RTP Company RTP 800 TFE 20 LP Acetal (POM), PTFE Lubricated |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D 648 |
| RTP Company RTP 800 TFE 5 HB Acetal (POM), PTFE Lubricated - UL94 HB The RTP 800 TFE Series materials are acetals containing PTFE lubricant. These products offer moldability and wear resistance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ISO 75 |
| Radici Heraform® R 900 Acetal Copolymer Standard grade for injection molding of details with high mechanical requirement.Information provided by Radici group. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ISO 75-1, -2 |
| MT8U05 POM, Medical Technology Hostaform« acetal copolymer grade MT8U05 is a special grade developed for medical industry applications containing low residual monomers and no animal products. The material can be identified by U.. |
|||