Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 230 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
RheTech Products F4702-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
Applications: Exterior door moldingsRigid bumper coversInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ISO 75-1, -2
Celanese Vandar® 4602Z PBT  (Unverified Data**)
4602Z is an unfilled thermoplastic alloy with good weatherability and chemical resistance.Unreinforced, good chemical resistanceInformation provided by Celanese
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
RheTech Products HP532-00 20% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Natural
Applications: Interior trimCenter tail light bezelPackage trayInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Hyosung Topilene J700 PP
J700 Injection General HomopolymerApplications: General injectionCharacteristics:ProcessabilityStiffnessInformation provided by Hyosung Corporation
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Unannealed; ASTM D648
Global PP-1126-NK Polypropylene Homopolymer
Description-transparency, high stiffness, high heat resistantApplications- food applicationsInformation provided by Global Polymers Corporation.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 6.40 mm
230 °F

@Thickness 0.252 in
Unannealed; ASTM D648
LG Chemical XR440 ABS, Low Emission High Heat ABS
Feature: Injection Molding Grade, Low Emission High Heat ABSApplication: Automotives Interior housingCAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Chemical
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648 B
Metabolix Mirelâ„¢ P4001 Sheet Extrusion Grade Bioplastic
Mirelâ„¢ P4001 is a general purpose, high melt strength material suitable for cast sheet extrusion. Mirelâ„¢ P4001 is designed for a wide range of sheet applications including gift cards, prom..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Asia Pacific)
LNP* Lubricomp* KG002 is a compound based on Acetal Copolymer resin containing Graphite Powder. Added features of this material include: Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Europe-Africa-Middle East)
Flame Retardant, Impact Modified, Opaque, Designed for outdoor telecommunication enclosure applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP DF0081PI PC (Asia Pacific)
LNP* Thermocomp* DF0081PI is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, good flatness, Non-Brominated & ..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific)
LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Xenoy® XD1575S PBT+PC (Europe-Africa-Middle East)
XENOY XD1575S is a high flow PC+PBT blend with good impact properties and good resistance to occasional solvent and gasoline contact. XENOY XD1575S has been specially developed for coated exterior b..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
SCG Chemicals EL-Proâ„¢ P600F Polypropylene Film Resin
Key Characteristics:Good optical propertiesHigh productivityGood openability with 3000 ppm slip agent and 2700 ppm antiblocking agentRecommended Applications:Water quenched blown film for food and a..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
SCG Chemicals EL-Proâ„¢ P740J Polypropylene Injection Molding
Key Characteristics:Good flowabilityGood processabilityHigh stiffnessRecommended Applications:Automotive, motorcycle and electrical appliance parts that require good flowability such as automotive t..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Unannealed; ASTM D648
Chase Plastics CP Pryme® A130 ABS, 30% Glass Fiber Reinforced
Features: Glass fiber reinforcementInjection moldingForm: PelletsInformation provided by Chase Plastics.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Tipco Tipcolene® FPT 40 - 40% Talc Reinforced Polypropylene Homopolymer Compound
40% Talc Reinforced PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 3716 is a 12% talc filled copolymer polypropylene product. Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
120°C per hour; ISO 752
Total PPH 4026 Polypropylene Homopolymer, Film
Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is in..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
A. Schulman POLYFORT™ FPP 1477 Mineral Filled, General-Purpose Polypropylene
DescriptionPolyfort® FPP 1477 is a 20% mineral filled, general-purpose polypropylene.Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Aclo Accucomp Polypropylene CPO425BAV Automotive Approved Copolymer Expandable Grade
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Aclo Accutech Polypropylene Homopolymer HP0336C30L Calcium Reinforced
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Aclo Accutech Polypropylene Homopolymer HP0339C40L1 Calcium Reinforced
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Arkema Group Cristamid® MS 1100 Semi-Aromatic Nylon (PASA) (Conditioned)
Designation ISO 1874-PA12/xx,MHLR,12-020Semi-aromatic polyamide (PASA) grade for injection molding and tubes extrusion.Transparency even thick. High resistance to environmental stress cracking. Good..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Aaron Industries AAROPRENE® CFIPP 2030 High Impact Calcium Carbonate Filled Polypropylene
AAROPRENE® CFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
120°C/h; ISO 75/1
Polykemi AB POLYfill PPC T1020 Polypropylene Copolymer, Mineral Reinforced
Information provided by Polykemi AB
Deflection Temperature at 0.46 MPa (66 psi) 110 - 215 °C
230 - 419 °F
Average value: 176 °C Grade Count:30
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and..
Deflection Temperature at 0.46 MPa (66 psi) 110 °C

@Thickness 6.40 mm
230 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Noryl EN212 PPE+PS
Extrusion grade. 212F (100C) DTUL. UL94 V-1 rated.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648
Ineos H35G-00 Polypropylene Homopolymer
This is a general purpose homopolymer for injection molding applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsC..