Polymer Property : Linear Mold Shrinkage = 0.0030 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
Ovation Polymers Opnyl OP66GF33 Nylon 66, 33% Glass Reinforced, Dry
Nylon 66 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the ..
Linear Mold Shrinkage 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
Polymerization Shrinkage
Premix Premi-Glas® 1240-20 Fiberglass Reinforced Thermoset Thick Molding Compound
Premi-Glas® 1240-20 is a fiberglass reinforced thermoset Thick Molding Compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st..
Linear Mold Shrinkage 0.0015 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0030 in/in

@Thickness 0.126 in
ASTM D 955
RTP Company RTP 303 TFE 15 SI 2 Polycarbonate (PC) Glass Fiber - PTFE Lubricated - Silicone Lubricated
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 4405.3 High Temperature Nylon (HTN), Glass Fiber
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 4705 Polytrimethylene Terephthalate (PTT), Glass Fiber
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 602 Acrylonitrile Butadiene Styrene (ABS), Glass Fiber
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 602 FR Acrylonitrile Butadiene Styrene (ABS), Glass Fiber - Flame Retardant - UL94 V-0
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Polymer Resources PC-G30-[color]-1 Polycarbonate, 30% Glass Reinforced with Mold Release
Polycarbonate, 30% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
ASTM D 955
RTP Company VLF 84007 Polyphthalamide (PPA), Long Glass Fiber - Heat Stabilized
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Lehmann & Voss LUVOCOM® 1106-7033 Polyether imide, with carbon fiber
Applications: High-strength and high-stiff parts; low coefficient of expansion.High continuous use and heat distortion temperature. Non flammable.High dimensionally stable precision parts.Electrical..
Linear Mold Shrinkage 0.00050 - 0.0030 cm/cm
0.00050 - 0.0030 in/in
Lehmann & Voss LUVOCOM® 1301-7294/BL PPS, linear, with glass fiber
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemic..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Lehmann & Voss LUVOCOM® 1-7488 Polyamide 66, with carbon fiber, heat stabilized
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.High dimensionally stable prec..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Lehmann & Voss LUVOCOM® 1-7893/GY Polyamide 66, with carbon fiber, heat stabilized
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Kolon KOPA® KN135HB30HI Multi Reinforced Nylon 6
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
PlastxWorld CEVIAN® EG106 ABS
Inherently Static Dissipative and Glass Fiber reinforced ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plastx..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company ESD C 1005 Polybutylene Terephthalate (PBT), Glass Fiber - ESD Protection - Electrically Conductive
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 1305 P-1 Polyphenylene Sulfide (PPS), Glass Fiber
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0030 in/in

@Thickness 0.126 in
ASTM D 955
RTP Company RTP 1501-40D Polyether-Ester Block Copolymer (TEEE / COPE); Glass Fiber
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D 955
RTP Company RTP 200 TC-C-30 FR Nylon 6/6 (PA), Thermally Conductive - Electrically Conductive - Flame Retardant
Preliminary Data Sheet
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 2299 X 108578 C Polyetheretherketone (PEEK), Long Glass Fiber
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 283 D TFE 15 Nylon 6/12 (PA), Carbon Fiber - PTFE Lubricated
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 2577
Polyram RamOfin PPH308G50 Polypropylene, 50% Glass Fiber, Impact Modified
50% Glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applications.Information provided by Polyram.
Linear Mold Shrinkage 0.0025 - 0.0030 cm/cm
0.0025 - 0.0030 in/in
Bulk Molding Compounds BMC T14 General Purpose Molding Compound
BMC T14 is a general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T14 is well suited for injection, transfer or compression molding of intricate parts. Typica..
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
ASTM D-955
Axiall 7181 Rigid PVC, Extrusion
Georgia Gulf 7181 is a special purpose rigid PVC profile extrusion compound designed for applications requiring the following properties: WeatherabilityImpact StrengthDimensional StabilityFlame Ret..
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
IS 13411-1992
Amity Thermosets ATO 1510 Phenolic Molding Glass fiber Filler, Compression Molded
Characteristics:Shock resistantElectrical low lossHigh mechanical strengthHeat stableHigh electrical insulationDimensional stabilityGood mechanical tension bearing strengthMedium copper adhesionColo..
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Cheng Yu Plastic A706G15 SAN, 15% Glass Fiber
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 4005 TFE 5 Polyphthalamide (PPA), Glass Fiber Reinforced - PTFE Lubricated
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 4407 High Temperature Nylon (HTN), Glass Fiber
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0020 - 0.0030 in/in

@Thickness 0.125 in
ASTM D 955
RTP Company VLF 80205 EM HS Nylon 6/6 (PA), Long Glass Fiber - Easy Molding - Heat Stabilized