Overview of materials for Polypropylene with 60% Glass Fiber Filler

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 60% Glass Fiber Filler
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Polypropylene with 60% Glass Fiber Filler.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.15 - 1.50 g/cc	0.0415 - 0.0542 lb/in³	Average value: 1.43 g/cc Grade Count:19
Filler Content	60.0 %	60.0 %	Average value: 60.0 % Grade Count:3
Linear Mold Shrinkage	0.00100 - 0.00600 cm/cm	0.00100 - 0.00600 in/in	Average value: 0.00376 cm/cm Grade Count:4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	117 - 280 MPa	17000 - 40600 psi	Average value: 151 MPa Grade Count:11
	80.0 - 90.0 MPa @Temperature 80.0 - 80.0 °C	11600 - 13100 psi @Temperature 176 - 176 °F	Average value: 85.3 MPa Grade Count:4
Tensile Strength, Yield	16.5 - 150 MPa	2400 - 21800 psi	Average value: 111 MPa Grade Count:7
Elongation at Break	1.00 - 3.00 %	1.00 - 3.00 %	Average value: 1.81 % Grade Count:17
	2.00 - 2.10 % @Temperature 80.0 - 80.0 °C	2.00 - 2.10 % @Temperature 176 - 176 °F	Average value: 2.03 % Grade Count:4
Modulus of Elasticity	6.30 - 25.1 GPa	914 - 3640 ksi	Average value: 14.1 GPa Grade Count:16
	9.10 - 9.50 GPa @Temperature 80.0 - 80.0 °C	1320 - 1380 ksi @Temperature 176 - 176 °F	Average value: 9.40 GPa Grade Count:4
Flexural Yield Strength	28.3 - 420 MPa	4100 - 60900 psi	Average value: 215 MPa Grade Count:18
	134 - 140 MPa @Temperature 80.0 - 80.0 °C	19400 - 20300 psi @Temperature 176 - 176 °F	Average value: 137 MPa Grade Count:4
Flexural Modulus	2.41 - 24.1 GPa	350 - 3500 ksi	Average value: 13.0 GPa Grade Count:18
	9.50 - 11.0 GPa @Temperature 80.0 - 80.0 °C	1380 - 1600 ksi @Temperature 176 - 176 °F	Average value: 10.2 GPa Grade Count:4
Izod Impact, Notched	0.320 - 3.42 J/cm	0.600 - 6.41 ft-lb/in	Average value: 2.36 J/cm Grade Count:7
Charpy Impact Unnotched	4.50 - 8.00 J/cm²	21.4 - 38.1 ft-lb/in²	Average value: 6.56 J/cm² Grade Count:8
	4.50 - 9.00 J/cm² @Temperature -30.0 - -20.0 °C	21.4 - 42.8 ft-lb/in² @Temperature -22.0 - -4.00 °F	Average value: 6.50 J/cm² Grade Count:7
Charpy Impact, Notched	1.10 - 4.80 J/cm²	5.24 - 22.8 ft-lb/in²	Average value: 2.98 J/cm² Grade Count:10
	0.900 - 5.00 J/cm² @Temperature -30.0 - -20.0 °C	4.28 - 23.8 ft-lb/in² @Temperature -22.0 - -4.00 °F	Average value: 3.24 J/cm² Grade Count:8

Thermal Properties	Metric	English	Comments
Melting Point	160 - 170 °C	320 - 338 °F	Average value: 166 °C Grade Count:9
Deflection Temperature at 1.8 MPa (264 psi)	85.0 - 175 °C	185 - 347 °F	Average value: 154 °C Grade Count:17

Processing Properties	Metric	English	Comments
Processing Temperature	30.0 - 270 °C	86.0 - 518 °F	Average value: 158 °C Grade Count:7
Die Temperature	240 - 250 °C	464 - 482 °F	Average value: 245 °C Grade Count:7
Melt Temperature	199 - 270 °C	390 - 518 °F	Average value: 239 °C Grade Count:10
Mold Temperature	37.8 - 90.0 °C	100 - 194 °F	Average value: 72.2 °C Grade Count:3
Drying Temperature	80.0 - 100 °C	176 - 212 °F	Average value: 91.7 °C Grade Count:9
Moisture Content	0.0200 - 0.200 %	0.0200 - 0.200 %	Average value: 0.174 % Grade Count:7
Injection Pressure	60.0 - 140 MPa	8700 - 20300 psi	Average value: 92.9 MPa Grade Count:9