Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 134 MPa | 19400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Cycolac® INP572 ABS High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to pro.. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycolac® INP572 ABS+SAN High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to pro.. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific) |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | ASTM D790 |
Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK)
(Unverified Data**) Ketaspire KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear res.. |
|||
Flexural Yield Strength | 133.76 MPa | 19400 psi | |
Abatron AboCast 8-13/Abocure 8-13 Epoxy
(discontinued **) 2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/12.80 ratio (pbw); Gel time, 100 g (3.5 oz.): 53 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°.. |
|||
Flexural Yield Strength | 133.76 MPa | 19400 psi | |
Abatron AboCast 8-14/Abocure 8-14 Epoxy
(discontinued **) 2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/12.10 ratio (pbw); Gel time, 100 g (3.5 oz.): 63 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°.. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | ASTM D790 |
Global AS-320-PC Acrylonitrile Styrene, High Chemical/High Heat Resistance Grade Description-transparent, medium impact resistance, high hardness, good stiffness, high heat resistance, good chemical resistanceApplications-sanitary products, electrical partsInformation provided b.. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | ASTM D790 |
Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK) KetaSpire® KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear.. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF VF004S SUPER TOUGH NYLON (Europe-Africa-Middle East) LNP* THERMOTUF* VF004S is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Yield Strength | 134 MPa | 19400 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 8325 Polycarbonate High viscosity injection molding and extrusion grade with 20% standard glass fibers and easy mold release, high strength and stiffness.Information provided by Bayer.As of 1 September 2015, Bayer Mat.. |
|||
Flexural Yield Strength | 134 - 140 MPa @Temperature 80.0 - 80.0 °C |
19400 - 20300 psi @Temperature 176 - 176 °F |
Average value: 137 MPa Grade Count:4 |
Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i.. |