Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 5.00 - 90.0 MPa @Temperature -40.0 - 160 °C |
725 - 13100 psi @Temperature -40.0 - 320 °F |
Average value: 38.8 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Tensile Strength, Ultimate | 5.00 - 90.0 MPa @Strain 2.00 - 10.0 % |
725 - 13100 psi @Strain 2.00 - 10.0 % |
Average value: 38.8 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Tensile Strength, Ultimate | 45.0 - 90.0 MPa @Temperature 60.0 - 150 °C |
6530 - 13100 psi @Temperature 140 - 302 °F |
Average value: 65.0 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Tensile Strength, Ultimate | 34.5 - 90.0 MPa | 5000 - 13100 psi | Average value: 52.7 MPa Grade Count:35 |
Overview of materials for Polyphenylene Ether, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Molded". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Ultimate | 48.0 - 90.0 MPa | 6960 - 13100 psi | Average value: 72.6 MPa Grade Count:7 |
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ.. |
|||
Tensile Strength, Ultimate | 50.0 - 90.0 MPa | 7250 - 13100 psi | Average value: 73.5 MPa Grade Count:7 |
Overview of materials for Nylon 66, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Ultimate | 22.0 - 90.0 MPa | 3190 - 13100 psi | Average value: 45.3 MPa Grade Count:27 |
Overview of materials for Polyethylene Terephthalate (PET), Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Unreinforced". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 43.1 - 90.0 MPa | 6250 - 13100 psi | Average value: 75.5 MPa Grade Count:38 |
Overview of materials for Nylon 6, Cast This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Tensile Strength, Ultimate | 50.0 - 90.0 MPa @Temperature 60.0 - 150 °C |
7250 - 13100 psi @Temperature 140 - 302 °F |
Average value: 71.3 MPa Grade Count:2 |
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc.. |
|||
Tensile Strength, Ultimate | 80.0 - 90.0 MPa @Temperature 80.0 - 80.0 °C |
11600 - 13100 psi @Temperature 176 - 176 °F |
Average value: 85.3 MPa Grade Count:4 |
Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i.. |