Polymer Property : Tensile Strength, Ultimate = 13100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	5.00 - 90.0 MPa @Temperature -40.0 - 160 °C	725 - 13100 psi @Temperature -40.0 - 320 °F	Average value: 38.8 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim..
Tensile Strength, Ultimate	5.00 - 90.0 MPa @Strain 2.00 - 10.0 %	725 - 13100 psi @Strain 2.00 - 10.0 %	Average value: 38.8 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim..
Tensile Strength, Ultimate	45.0 - 90.0 MPa @Temperature 60.0 - 150 °C	6530 - 13100 psi @Temperature 140 - 302 °F	Average value: 65.0 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45..
Tensile Strength, Ultimate	34.5 - 90.0 MPa	5000 - 13100 psi	Average value: 52.7 MPa Grade Count:35
Overview of materials for Polyphenylene Ether, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Molded". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate	48.0 - 90.0 MPa	6960 - 13100 psi	Average value: 72.6 MPa Grade Count:7
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ..
Tensile Strength, Ultimate	50.0 - 90.0 MPa	7250 - 13100 psi	Average value: 73.5 MPa Grade Count:7
Overview of materials for Nylon 66, Nucleated This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat..
Tensile Strength, Ultimate	22.0 - 90.0 MPa	3190 - 13100 psi	Average value: 45.3 MPa Grade Count:27
Overview of materials for Polyethylene Terephthalate (PET), Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Unreinforced". Each property range of values reported is minimum and m..
Tensile Strength, Ultimate	43.1 - 90.0 MPa	6250 - 13100 psi	Average value: 75.5 MPa Grade Count:38
Overview of materials for Nylon 6, Cast This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW..
Tensile Strength, Ultimate	50.0 - 90.0 MPa @Temperature 60.0 - 150 °C	7250 - 13100 psi @Temperature 140 - 302 °F	Average value: 71.3 MPa Grade Count:2
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc..
Tensile Strength, Ultimate	80.0 - 90.0 MPa @Temperature 80.0 - 80.0 °C	11600 - 13100 psi @Temperature 176 - 176 °F	Average value: 85.3 MPa Grade Count:4
Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i..