Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, DAM

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, DAM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® 21SPF is general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grade offers a well-balanced combination of engineering properties characterized by high strength; rigidity; good toughness; high melt point; good surface lubricity; abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 21SPF resin permits product of molded parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal and military specifications for premium-quality, general-purpose PA66 resins. Vydyne 21SPF resin is internally and externally lubricated for improved machine feed and exceptional mold release. It is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity. Vydyne 21SPF can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be check against specifications before implementing shorter molding cycles on a routine product basis.Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass FiberMineral Additive:Lubricant Features: Good Mold ReleaseHigh RigidityHigh Strength High Tensile Strength LubricatedOutstanding Surface Finish Uses:Automotive Under the HoodGearsHousingsLawn and Garden EquipmentMetal ReplacementPower/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ISO 1183
Water Absorption	1.2 %	1.2 %	24 hrs; ISO 62
Moisture Absorption at Equilibrium	2.4 %	2.4 %	Equilibrium at 50%rh; ISO 62
Linear Mold Shrinkage	0.020 cm/cm @Thickness 2.00 mm	0.020 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.020 cm/cm @Thickness 2.00 mm	0.020 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527-2
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Elongation at Break	20 %	20 %	ISO 527-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-2
Tensile Modulus	3.30 GPa	479 ksi	ISO 527-2
Flexural Strength	105 MPa	15200 psi	ISO 178
Flexural Modulus	3.30 GPa	479 ksi	ISO 178
Poissons Ratio	0.40	0.40	ISO 527-2
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO 180
	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1EU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1EU
Charpy Impact, Notched	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179/1EA
	0.600 J/cm² @Temperature 23.0 °C	2.86 ft-lb/in² @Temperature 73.4 °F	ISO 179/1EA

Thermal Properties	Metric	English	Comments
CTE, linear	10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359-2
CTE, linear, Transverse to Flow	10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C	5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F	ISO 11359-2
Melting Point	260 °C	500 °F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F	ISO 75-B/2
Deflection Temperature at 1.8 MPa (264 psi)	72.0 °C	162 °F	ISO 75-A/2
UL RTI, Electrical	130 °C @Thickness 0.710 mm	266 °F @Thickness 0.0280 in	UL 746
	130 °C @Thickness 0.400 mm	266 °F @Thickness 0.0157 in	UL 746
	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	UL 746
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical with Impact	75.0 °C @Thickness 0.400 mm	167 °F @Thickness 0.0157 in	UL 746
	75.0 °C @Thickness 0.710 mm	167 °F @Thickness 0.0280 in	UL 746
	75.0 °C @Thickness 1.50 mm	167 °F @Thickness 0.0591 in	UL 746
	75.0 °C @Thickness 3.00 mm	167 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical without Impact	75.0 °C @Thickness 0.400 mm	167 °F @Thickness 0.0157 in	UL 746
	85.0 °C @Thickness 0.710 mm	185 °F @Thickness 0.0280 in	UL 746
	85.0 °C @Thickness 1.50 mm	185 °F @Thickness 0.0591 in	UL 746
	85.0 °C @Thickness 3.00 mm	185 °F @Thickness 0.118 in	UL 746
Flammability, UL94	V-2 @Thickness 0.400 mm	V-2 @Thickness 0.0157 in
	V-2 @Thickness 0.710 mm	V-2 @Thickness 0.0280 in
	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in
Oxygen Index	26 %	26 %	ASTM D2863
Glow Wire Test	700 °C @Thickness 0.710 mm	1290 °F @Thickness 0.0280 in	Ignition Temperature; IEC 60695-2-13
	700 °C @Thickness 1.50 mm	1290 °F @Thickness 0.0591 in	Ignition Temperature; IEC 60695-2-13
	700 °C @Thickness 3.00 mm	1290 °F @Thickness 0.118 in	Ignition Temperature; IEC 60695-2-13
	800 °C @Thickness 0.710 mm	1470 °F @Thickness 0.0280 in	Flammability Index; IEC 60695-2-12
	800 °C @Thickness 1.50 mm	1470 °F @Thickness 0.0591 in	Flammability Index; IEC 60695-2-12
	930 °C @Thickness 3.00 mm	1710 °F @Thickness 0.118 in	Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm @Thickness 0.750 mm	1.00e+10 ohm-cm @Thickness 0.0295 in	IEC 60093
Dielectric Strength	26.0 kV/mm @Thickness 1.00 mm	660 kV/in @Thickness 0.0394 in	IEC 60243
Arc Resistance	120 - 179 sec @Thickness 3.00 mm	120 - 179 sec @Thickness 0.118 in	ASTM D495
Comparative Tracking Index	>= 600 V @Thickness 3.00 mm	>= 600 V @Thickness 0.118 in	IEC 60112
Hot Wire Ignition, HWI	7.0 - 15 sec @Thickness 0.710 mm	7.0 - 15 sec @Thickness 0.0280 in	UL 746
	15 - 30 sec @Thickness 1.50 mm	15 - 30 sec @Thickness 0.0591 in	UL 746
	15 - 30 sec @Thickness 3.00 mm	15 - 30 sec @Thickness 0.118 in	UL 746
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.710 mm	>= 120 arcs @Thickness 0.0280 in	UL 746A
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	UL 746
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	UL 746
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min	0.000 - 0.394 in/min	UL 746

Processing Properties	Metric	English	Comments
Processing Temperature	285 - 300 °C	545 - 572 °F	Melt
Rear Barrel Temperature	260 - 280 °C	500 - 536 °F
Middle Barrel Temperature	270 - 285 °C	518 - 545 °F
Front Barrel Temperature	280 - 290 °C	536 - 554 °F
Nozzle Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	65.0 - 95.0 °C	149 - 203 °F
Drying Temperature	<= 70.0 °C	<= 158 °F