Polymer Property : Tensile Strength, Yield = 88.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
Nylene® 603 Nylon 6, Extrusion Grade Dry as molded. Extrusion grade. Nylene 603 is a plasticized, high residual monomer resin designed for extrusion applications requiring excellent flexibility, high strength and good abrasion resist..
Tensile Strength, Yield	88.0 MPa	12800 psi	50 mm/min; ASTM D638
Ovation Polymers Uttap SF 600 Polyethersulfone Polyether Sulfone Resin-Medium Viscosity, unreinforced standard grade for Easy Injection Molding.Information provided by Ovation Polymers
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC (Asia Pacific) LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Tensile Strength, Yield	88.0 MPa @Temperature 23.0 °C	12800 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® 101L BKB009 Nylon 66 (Unverified Data**) Zytel® 101L BKB009 is a lubricated polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
Manifattura Cattaneo PEEK Polyetheretherketone Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
Tensile Strength, Yield	88.0 MPa @Strain 0.200 %, Temperature 1095 Â°C	12800 psi @Strain 0.200 %, Temperature 2003 Â°F
Haynes 188 alloy, hot rolled and 1175Â°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	88.0 MPa	12800 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl PX6592 PPE+PS (Asia Pacific) 20% glass filled, PPO/HIPS alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield	88.0 MPa	12800 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL S100G20 PPE+PS (Asia Pacific)
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Asia Pacific) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific) LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Strength, Yield	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM D9065 PEI (Asia Pacific) Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527 type 1 A
Solvay TECHNYLÂ® A 217 PA66, DRY Description: TECHNYL Â® A 217 is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection molding. It is available in black color.Benefits: This product offers all the prim..
Tensile Strength, Yield	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Tensile Strength, Yield	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 55/55 with low toxicity, smoke and flame evolution.
Tensile Strength, Yield	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength, Yield	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Asia Pacific) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength, Yield	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength, Yield	88.0 MPa	12800 psi	D638
Zhejiang Juner 301-G15 15% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, ..
Tensile Strength, Yield	88.0 MPa	12800 psi	50 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6000 HWCP Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527
Eurostar Star L PA66 D91 PA66, Aramid Fiber Filled, Injection Molded Star L PA66 D91 is a PTFE lubricated, Aramid Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF BLK Nylon 66, Conditioned Vydyne® 21SPF BLK is a, general-purpose PA66 resin used for extrusion-compounding. Available in black, it is designed principally for injection-molding fabrication. This grade offers a well-balance..
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, DAM Vydyne® 21SPF is general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grade offers a well-balanced combination of engineering propert..
Tensile Strength, Yield	88.0 MPa	12800 psi	50mm/min; ISO 527
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Tensile Strength, Yield	88.0 MPa	12800 psi	50mm/min; ISO 527
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength, Yield	88.0 MPa	12800 psi	Dry; ASTM D638
Asahi Kasei Leona® CR301 Nylon 66 Suitable for a switch insulator. Low abrasion and superior electrical properties.Applications:Sliding switch insulators Information provided by Asahi Kasei
Tensile Strength, Yield	88.0 MPa	12800 psi	SABIC - Japan Method
SABIC Innovative Plastics NORYL PX2944 PPE+HIPS (Asia Pacific) PPE/PS, GF20%, high heat, non-FR
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, DAM Vydyne® 21SPF1 is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding applications with the added benefits of improved flow during the molding ..