Polymer Property : Tensile Strength at Break = 60.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Cycolac® INP581 ABS High flow, low molecular weight SAN. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for..
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527
Nilit FRIANYL B63 SG40 Nylon 6 for injection molding, 40% mineral filled Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527
Nilit RECONYL B S Recycled nylon 6 for injection molding Recycled nylon 6 for injection molding, impact modified (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL6033 PC (Europe-Africa-Middle East) PC-Siloxane copolymer with good processability.Very low temp. ductility, UV-Stabilized, UL94 V1 rated in white colors only.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® ML7689 PC Copolymer (Europe-Africa-Middle East) Lexan* ML7689 polycarbonate (PC) siloxane copolymer resin IS a high viscosity injection molding (IM) grade WITH good processability, offering opportunities FOR shorter IM CYCLE times compared TO sta..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® XHT1143 PC (Asia Pacific) XHT1143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is the lowest heat, UV stabilized product in the LEXAN* XHT portfolio. It is available in a range of opaque and limited ..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® XHT1143 PC (Europe-Africa-Middle East) XHT1143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is the lowest heat, UV stabilized product in the LEXAN* XHT portfolio. It is available in a range of opaque and limited ..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Tensile Strength at Break	60.0 MPa	8700 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to Lexan* XHT2141 resin. It is available in a range of opaque and limited transparent colo..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Tensile Strength at Break	60.0 MPa	8700 psi	ASTM D638
Polymer Resources NY66-IM1-[color]-H Nylon 66, Medium Impact Modified, Heat Stabilized Nylon 66, Medium Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Ny..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HPH4404 PPC+PC High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril..
Tensile Strength at Break	60.0 MPa	8700 psi	ASTM D683
Loxim 210 01HB Polybutylene Terephthalate Information provided by Loxim Industries
Tensile Strength at Break	60.0 MPa	8700 psi
LATI Latilub 57-10T Y/15 PPA, Aramid Reinforced Self-lubricating product based on Semi-aromatic polyamide (PPA). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La..
Tensile Strength at Break	60.0 MPa	8700 psi
LATI Latilub 85-10T G/30 PES, 30% Glass Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyether Sulfone (PES). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu..
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 50 H2 PA6, DRY Description: TECHNYLÂ® C 50H2 is a unreinforced melamine cyanurate flame retarded polyamide 6. This product is heat stabilized and can be used for injection molding and extrusion processes. This p..
Tensile Strength at Break	60.0 MPa @Temperature 80.0 Â°C	8700 psi @Temperature 176 Â°F	50 mm/min, 1A; ISO 527
SABIC Innovative Plastics SABIC STAMAX 30YK270 PP SABICÂ® STAMAX 30YK270 is a 30% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stif..
Tensile Strength at Break	60.0 MPa	8700 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON DX05499 PC (Asia Pacific) LNP STAT-KON* DX05499 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	60.0 MPa	8700 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics XenoyÂ® X4810 PBT+PC Xenoy X4810 is a hydrostable, High Modulus Ductile PC/PBT blend. This resin provides low temperature (below 0C) ductile impact behaviour, high chemical resistance, very low creep, low CTE, excellent..
Tensile Strength at Break	60.0 MPa	8700 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP KF004AL Acetal Homopolymer LNP* THERMOCOMP* KF004AL is a compound based on Acetal Homopolymer resin containing 20% Glass Fiber. Added features of this material include: Low Extractible.
Tensile Strength at Break	60.0 MPa	8700 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL LTA1350 PPE+PS Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No..
Tensile Strength at Break	60.0 MPa	8700 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL ENV131 PPE+HIPS (Europe-Africa-Middle East) Noryl* ENV131 is an unfilled modified polyphenylene ether resin developed for extrusion process. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V1 rating ..
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527
Azdel Plus R300-B01 30% Continuous Random Fiber Mat / PP Resin Matrix AZDEL® R300-B01 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a polypropylene resin matrix. This composite material features high flow pr..
Tensile Strength at Break	60.0 MPa	8700 psi	0.2 in/min; ASTM Test
BASF Ultramid® 8260 40% Mineral Filled PA6 (Conditioned) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low..
Tensile Strength at Break	60.0 MPa @Temperature 80.0 °C	8700 psi @Temperature 176 °F	ASTM Test
BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in..
Tensile Strength at Break	60.0 MPa @Temperature 80.0 °C	8700 psi @Temperature 176 °F	50 mm/min, 1A; ISO 527
SABIC Innovative Plastics SABIC STAMAX 20YM240 PP SABIC® STAMAX 20YM240 is a 20% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 62455287.
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527-1/-2
DSM Akulon® K224-HPG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..