Polymer Property : Flexural Strength = 15200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	105 MPa	15200 psi	ASTM D-790
Plaskolite Optix® CA - 71 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Flexural Strength	105 MPa	15200 psi	ASTM D-790
Plaskolite West Optix® CP - 71 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
Flexural Strength	105 MPa	15200 psi
Plastcom SLOVAMID 6 FRM1X3 PA6, flame retardant FeaturesDetermined for electrotechnical use. Delivered in natural mode. PA 6 for injection moulding with reduced flammability, with nonhalogen flame retardant. Excellent fluidity of the material pre..
Flexural Strength	105 MPa	15200 psi
Plastcom SLOVASTER® B1 GF 6 HML PBT, 6% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 6 % glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending..
Flexural Strength	105 MPa	15200 psi	ISO 178
Polycasa SAN QUINN SAN sheets are characterized by good optical properties and a brilliant surface. The QUINN SAN range contains sheets that are easy to handle, to vacuum form, and show a very good dimensional s..
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOMÂ® 1105-7198/BK PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio..
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOMÂ® 1105-7835 PEEK, with glass fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Low warpage, isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts,..
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOMÂ® 1500-0871 Polysulfone, with glass spheres Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, ca..
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOMÂ® 20-0664 Polyphthalamide, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an..
Flexural Strength	105 MPa	15200 psi	1.5 mm/min; ISO 178:2001
Global EPP PA 6C Cast Polyamide 6 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Flexural Strength	105 MPa	15200 psi	1.5 mm/min; ISO 178:2001
Global EPP PA 6C HS BLUE Cast Polyamide 6 + UV and Heat Stabilizers Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOMÂ® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,..
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOMÂ® 80-8030 Polyacetal-copolymer, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically ..
Flexural Strength	105 MPa	15200 psi	ISO 178
Solvay TECHNYLÂ® B 50 H1 PA66/6, DRY Description: TECHNYLÂ® B 50H1 is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilized and is suitable for injection molding. This product is av..
Flexural Strength	105 MPa	15200 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific) LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Strength	105 MPa	15200 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DFD029 PC (Europe-Africa-Middle East) LNP* Stat-kon* DFD029 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant, Carbon Powder. Added features of this material include: Electrically Conductive, Flame Reta..
Flexural Strength	105 MPa	15200 psi	ASTM D790
Techmer ES HiFillÂ® PA6 L BK Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: LubricatedAppearance: BlackTPCI# 9356102Information provided by TP Composites, Inc.
Flexural Strength	105 MPa	15200 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible.
Flexural Strength	105 MPa	15200 psi	ISO 178-93
Wellman Wellamid® 21LH-NBK4 General Purpose Nylon 66 Description: General Purpose Nylon 66Information provided by Wellman.
Flexural Strength	105 MPa	15200 psi	ISO 178-93
Wellman Wellamid® GS1791-N2 5% Glass Sphere Reinforced, Natural Nylon 66 Description: Glass Sphere Reinforced, Natural Nylon 66Information provided by Wellman.
Flexural Strength	105 MPa	15200 psi	ISO 178-93
Wellman Wellamid® NY1599-BK Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman.
Flexural Strength	105 MPa	15200 psi	2 mm/min; ISO 178
Eurostar Starflam AFR200B PA66, Flame Retardant, Injection Molding Staramide AFR200B is an Unfilled, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	105 MPa	15200 psi
Lehmann & Voss LUVOCOM® 1700-7903 PPO, with glass fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance r..
Flexural Strength	105 MPa	15200 psi	ISO 178
Lucite International Diakon® CLG357 Acrylic Polymer Information provided by Lucite International
Flexural Strength	105 MPa	15200 psi	ISO 178
Lucite International Diakon® ST15G8 Toughened Acrylic Polymer The Diakon® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness. The grades in the Diakon® series can be processed by in..
Flexural Strength	105 MPa	15200 psi	ISO 178
Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, DAM Vydyne® 21SPF1 is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding applications with the added benefits of improved flow during the molding ..