Polymer Property : Tensile Strength, Yield = 12800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	88.0 MPa	12800 psi	50 mm/min; ASTM D638
Ovation Polymers Uttap SF 600 Polyethersulfone Polyether Sulfone Resin-Medium Viscosity, unreinforced standard grade for Easy Injection Molding.Information provided by Ovation Polymers
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC (Asia Pacific) LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	88.3 MPa	12800 psi	ASTM D638
LNP Lubricomp® EL-4030 Polyetherimide, PTFE Additive (discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
Manifattura Cattaneo PEEK Polyetheretherketone Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
Tensile Strength, Yield	88.0 MPa @Strain 0.200 %, Temperature 1095 Â°C	12800 psi @Strain 0.200 %, Temperature 2003 Â°F
Haynes 188 alloy, hot rolled and 1175Â°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Tensile Strength, Yield	88.0 MPa	12800 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield	88.3 MPa	12800 psi	ASTM D638
Techmer ES LuriblendÂ® PA6 GF15 TL15 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 15% Filler by WeightAdditive: Heat Stabilized and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Heat Stab..
Tensile Strength, Yield	88.3 MPa	12800 psi	ASTM D638
Techmer ES PlastiblendÂ® PSU CR X Availability: North AmericaForms: PelletsAdditive: TPU Impact Modifier Features: Impact ModifiedInformation provided by TP Composites, Inc.
Tensile Strength, Yield	88.3 MPa	12800 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® GR-4020 ABS, 20% Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	88.3 MPa	12800 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® GR-4020 ABS, 20% Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	88.3 MPa	12800 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VG-4920 ABS, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	88.3 MPa	12800 psi	ASTM D638
Samyang TribitÂ® 1500GN15 Polybutylene Terephthalate, 15% Glass Reinforced, Flame Retardant Characteristics:G/F reinforcedFlame retardantHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A..
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength, Yield	88.0 MPa	12800 psi	Type I, 10 mm/min; SABIC - Japan Method
SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump..
Tensile Strength, Yield	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant.
Tensile Strength, Yield	88.3 MPa	12800 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® NH-3204G PC, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	88.3 MPa	12800 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® NH-3204G PC, Glass Filled FR Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	88.0 MPa	12800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Tensile Strength, Yield	88.3 MPa	12800 psi	ASTM 638
PlastxWorld CEVIAN® VGR30 30% GF ABS Glass fiber reinforced ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Tensile Strength, Yield	88.0 MPa	12800 psi	D638
Zhejiang Juner 301-G15 15% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, ..
Tensile Strength, Yield	88.3 MPa	12800 psi	ASTM D638
Cheng Yu Plastic N66C2 Nylon 66, 20% Mineral Reinforced
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527
Eurostar Star L PA66 D91 PA66, Aramid Fiber Filled, Injection Molded Star L PA66 D91 is a PTFE lubricated, Aramid Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF BLK Nylon 66, Conditioned Vydyne® 21SPF BLK is a, general-purpose PA66 resin used for extrusion-compounding. Available in black, it is designed principally for injection-molding fabrication. This grade offers a well-balance..
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, DAM Vydyne® 21SPF is general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grade offers a well-balanced combination of engineering propert..
Tensile Strength, Yield	88.0 MPa	12800 psi	50mm/min; ISO 527
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique ..
Tensile Strength, Yield	88.0 MPa	12800 psi	Dry; ASTM D638
Asahi Kasei Leona® CR301 Nylon 66 Suitable for a switch insulator. Low abrasion and superior electrical properties.Applications:Sliding switch insulators Information provided by Asahi Kasei
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, DAM Vydyne® 21SPF1 is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding applications with the added benefits of improved flow during the molding ..