Toyobo Vylopet® EMC630 PET/PBT Blend

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET)
Manufacturer	Toyobo
Trade Name	VYLOPET®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Toyobo Vylopet® EMC630 PET/PBT Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Feature: Flame retardant V-0 UL 94 classApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, chemical & weather resistance, and processability.Information provided by Toyobo Co., Ltd

Physical Properties	Metric	English	Comments
Density	1.59 g/cc	0.0574 lb/in³	ASTM D792
Water Absorption	0.050 %	0.050 %	ASTM D570
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	95	95	ASTM D785
Tensile Strength, Ultimate	137 MPa	19900 psi	ASTM D638
Elongation at Break	2.2 %	2.2 %	ASTM D638
Flexural Yield Strength	206 MPa	29900 psi	ASTM D790
Flexural Modulus	9.80 GPa	1420 ksi	ASTM D790
Compressive Yield Strength	103 MPa	14900 psi	ASTM D695
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256
Taber Abrasion, mg/1000 Cycles	33	33	ASTM D1044

Thermal Properties	Metric	English	Comments
Melting Point	255 °C	491 °F	DSC
Deflection Temperature at 0.46 MPa (66 psi)	225 °C	437 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	ASTM D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Strength	25.0 kV/mm @Thickness 2.00 mm	635 kV/in @Thickness 0.0787 in	ASTM D149
Arc Resistance	80 sec	80 sec	ASTM D495
Comparative Tracking Index	215 V	215 V	IEC test