Styron EMERGEâ„¢ 5302 Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 5302 Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMERGEâ„¢ ABS 5302 is a black, 20% glass-filled ABS which is suitable for use in a wide variety of internal structural component applications in the information technology market. Applications: Information Technology Equipment and Consumer Electronics Printer Internal Components Structural Frames Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183B
Filler Content 20 %
20 %
Glass; ISO 5630-B
Linear Mold Shrinkage 0.0015 - 0.0025 cm/cm
0.0015 - 0.0025 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0035 - 0.0040 cm/cm
0.0035 - 0.0040 in/in
ISO 294-4
Melt Flow 1.6 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 1.6 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ISO 1133
5.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 5.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.0 MPa

@Thickness 4.00 mm
 10400 psi

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Tensile Strength, Yield 72.0 MPa

@Thickness 4.00 mm
 10400 psi

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Elongation at Break 2.0 %

@Thickness 4.00 mm
 2.0 %

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Elongation at Yield 2.0 %

@Thickness 4.00 mm
 2.0 %

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Tensile Modulus 6.10 GPa
885 ksi
1mm/min, 4mm injection molded, unannealed; ISO 527-2
Flexural Strength 115 MPa

@Thickness 4.00 mm
 16700 psi

@Thickness 0.157 in
 2mm/min, injection molded, unannealed; ISO 178
Flexural Modulus 6.20 GPa

@Thickness 4.00 mm
 899 ksi

@Thickness 0.157 in
 2mm/min, injection molded, unannealed; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/A
Charpy Impact, Notched 0.750 J/cm²
3.57 ft-lb/in²
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 50.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
CTE, linear, Transverse to Flow 94.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 52.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
unannealed; ISO 75-B
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
unannealed; ISO 75-A
Vicat Softening Point 106 °C
223 °F
50°C / 50N; ISO 306-B50
115 °C
239 °F
120°C / 10N; ISO 306-A120
Flammability, UL94 HB

@Thickness 1.00 - 2.50 mm
 HB

@Thickness 0.0394 - 0.0984 in
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Mold Temperature 20.0 - 60.0 °C
68.0 - 140 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 3 - 4 hour
3 - 4 hour