Polymer Property : Flexural Strength = 115 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	115 MPa	16700 psi	STN EN ISO 178
Plastcom SLOVALEN PH 69 GF 30 Polypropylene Homopolymer, 30% Glass Fiber FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP..
Flexural Strength	115 MPa	16700 psi	ASTM D790
PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Flexural Strength	115 MPa	16700 psi	ASTM D790
PolyOne Maxxam™ PPR-30G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Flexural Strength	115 MPa	16700 psi	ASTM D790
PolyOne Maxxam™ X MX5210-0030 RS Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Flexural Strength	115 MPa	16700 psi	ISO 178
Polycasa AKRYLON XT PMMA AKRYLON XT sheets have good optical properties and high quality surfaces. AKRYLON XT sheets also show excellent color and functional stability and can be used in contact with foodstuffs. AKRYLON XT ..
Flexural Strength	115 MPa	16700 psi	ASTM D790
Nilit Polynil® C50 PA66/6 Co-Polymer Description: NYLON 66/6 copolymerApplication: CompoundingInformation provided by NILIT.
Flexural Strength	115 MPa	16700 psi	ASTM D790
Nilit Polynil® C50L Externally Lubricated PA66/6 Description: Polynil C50L shows better surface finish, flow and elongation than a comparable homopolymer. Key characteristics: Excellent flowHigh elongationGood impact strengthGood overall mechanica..
Flexural Strength	115 MPa	16700 psi	ASTM D790
Nilit Polynil® P120 Medium Viscosity Nylon 66 Description: Medium viscosityApplication: MonofilamentInformation provided by NILIT.
Flexural Strength	115 MPa	16700 psi	ISO 178
Nilit FRIANYL A63 GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	115 MPa	16700 psi	ISO 178
Nilit FRIANYL A63 H-KV30 Nylon 6.6 for injection molding, 30% glass ball reinforced Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	115 MPa	16700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® JK500 PC+ABS (Asia Pacific) 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications.
Flexural Strength	115 MPa	16700 psi	Conditioned; ASTM D790
Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. Th..
Flexural Strength	115 MPa	16700 psi	2 mm/min; ISO 178
Hexion Bakelite™ PF 2774 Phenolic Formaldehyde Resin, Dishwasher Proof, Improved Electrical Properties, Low Shrinkage, UL Listed Phenolic molding compound, inorganically filled, glass fiber reinforced, increased dimensional stability, averaged notched impact strength, average heat resistance, improved electrical properties, U..
Flexural Strength	115 MPa	16700 psi
Lehmann & Voss LUVOCOMÂ® 1301-7661/RD PPS, linear, with glass fiber and PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Improved fr..
Flexural Strength	115 MPa	16700 psi	ISO 178
Kuraray Genestarâ„¢ N1002A-M41 Nylon Low friction unreinforced injection grade. Main Features:Low friction coefficientLow wearExamples of applications are:Friction and wear applicationGear and wheel
Flexural Strength	115 MPa	16700 psi	ISO 178
Lucite International DiakonÂ® CMG314V Acrylic Polymer Information provided by Lucite International
Flexural Strength	115 MPa	16700 psi
Lehmann & Voss LUVOCOMÂ® 1105-1330 PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio..
Flexural Strength	115 MPa	16700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL V02570 PPE+HIPS Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t..
Flexural Strength	115 MPa	16700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t..
Flexural Strength	115 MPa	16700 psi	ASTM D790
Techmer ES HiFillÂ® PA6 LE BK (Dry) Availability: North AmericaForms: PelletsAdditive: Lubricant and Nucleating AgentFeatures: Lubricated, Fast Molding Cycle, Good Processability, Low Extractables and NucleatedAppearance: BlackTPCI# 7..
Flexural Strength	115 MPa	16700 psi
SPS Guang Zhou POBUXâ„¢ 3001G10 Flame-retarded/GF10%-PBT Characteristic: Good flame retardance, high mechanical properties, high rigidity, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) ..
Flexural Strength	115 MPa	16700 psi	ASTM D790
Plenco 6582 Phenolic, Briquette, Transfer Molded PLENCO 06582 is a rubber modified phenolic molding compound, offering excellent heat resistant properties, along with improved mechanical strength at elevated temperatures. UL recognized under compo..
Flexural Strength	115 MPa	16700 psi	ISO 178-93
Wellman Wellamid® NY1599-N Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman.
Flexural Strength	115 MPa	16700 psi	GB/9341
Zhejiang Juner PA-A5 Flame-Retardant & Mineral Reinforced PA6 Applications: Mid-Grade CBInformation provided by Zhejiang Juner New Materials Co, Ltd.
Flexural Strength	115 MPa	16700 psi	ASTM D790
A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman.
Flexural Strength	115 MPa	16700 psi	ASTM D790
A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman.
Flexural Strength	<= 115 MPa	<= 16700 psi	3.5% flexure; ISO 178
Azoty Tarnow™ Tarnamid® T-27 MF30 Polyamide 6 - Mineral Reinforced 30% Mineral filled, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechani..
Flexural Strength	115 MPa	16700 psi	2mm/min; ISO 178
Teijin Panlite® G-3410H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 10 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci..
Flexural Strength	115 MPa	16700 psi	ASTM D790
Sumitomo Bakelite North America FM 4004F Fiberglass and Mineral Reinforced Phenolic Novolac FM 4004F is a fiberglass and mineral reinforced phenolic novolac compound with improved strength properties over FM 4004. This compound exhibits excellent dimensional stability and good strength at..