- Polymer Property : Dry Time = 3 hour
Polymer Property : Dry Time = 3 hour Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Polymer Resources TP-FR IM PBT, Impact Modified, Flame Retardant, Low Flow Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Ravago Manufacturing Americas Hylex® P1310LLT Polycarbonate Information provided by Ravago |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| PTS Trimid® N6-600 Medium Viscosity Extrusion Grade Nylon 6 Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| PTS Tristar® PC-10R-(22) 22 MFI Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Dry Time | 3 hour | 3 hour | Desiccant Dryer |
| ExxonMobil Santoprene® 121-80M300 Thermoplastic Rubber
(discontinued **) Description: A black thermoplastic high-flow elastomer for excellent injection molding performance with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloropren.. |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| PTS Tristar® PC-10R-(V) 10 MFI UV Stabilized Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized
(discontinued **) Similar to 3013A, but higher in molecular weight.Applications: Pipe fittings, rollers, exterior automotive parts.This product is not a part of the standard product line dated 2003. |
|||
| Dry Time | >= 3 hour | >= 3 hour | Not essential, drying time can be reduced when using vacuum ovens. |
| LATI LATAN 3E71 Polyoxymethylene Copolymer (POM) with Elastomer
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer |
| Celanese Zenite® 9140HT BK010 LCP
(discontinued **) Zenite® 9140HT BK010 is a 40% glass reinforced, black liquid crystal polymer resin having an excellent heat deflection temperature of 356°C.Celenese acquired the Zenite product line from DuPont in.. |
|||
| Dry Time | 3 - 6 hour | 3 - 6 hour | |
| LG Chemical LUCEL GB-325 Low Warpage POM, 25% Glass Bead Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Kolon DIAMAT® IH Description: DIAMAT® is a specially formulated high impact grade PMMA resin from KOLON. The acrylic composition results in an excellent balance of impact resistance and high modulus at reasonabl.. |
|||
| Dry Time | 3 - 6 hour | 3 - 6 hour | |
| LG Chemical LUCEL HI-525 High Impact POM, Unreinforced LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Dry Time | 3 - 6 hour | 3 - 6 hour | |
| LG Chemical LUCEL WK-320 Wear Resistant POM, 20% Mineral Filled, High Modulus LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 12 hours |
| LTL Color Compounds ColorFast® PBT100 PBT General purpose injection molding grade unfilled PBT with lubeAll information provided by LTL Color Compounders, Inc. |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| Mitsubishi Iupilon® S3000UR 16.5 MFI, UV Stabilized Polycarbonate With Release Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Kostat BK-STAT 7048BK ABS Compound BK-STAT Compounds are statically dissipative thermoplastics based on IDP (Inherently Dissipative Polymers) technology. This class of materials have distinctive advantages in hot spots and cleanline.. |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Kostat BK-STAT R048BK PS Compound BK-STAT Compounds are statically dissipative thermoplastics based on IDP (Inherently Dissipative Polymers) technology. This class of materials have distinctive advantages in hot spots and cleanline.. |
|||
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Samyang Triloy® 170 PC/PBT alloy Characteristics:Impact resistantChemical resistantDimensional stabilityProcessabilityFlame retardantApplications:Automotive bumperAutomotive outdoor handleAll information provided by Samyang |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Styron EMERGEâ„¢ 4702-8 Polycarbonate EMERGEâ„¢ PC 4702-8 advanced resin is formulated with 20% glass fiber and a proprietary flame retardant package. It provides good ignition resistance, rigidity, dimension stability and heat resi.. |
|||
| Dry Time | 3 hour | 3 hour | |
| Teknor Apex Sarlink® 3145D Thermoplastic Elastomer A high hardness, multi-purpose thermoplastic elastomer featuring excellent compression set and high temperature performance. Sarlink® 3145D can be processed by injection blow molding, molding or .. |
|||
| Dry Time | 3 hour | 3 hour | |
| RTP Company RTP 2205 HF TFE 15 Polyetheretherketone (PEEK), Glass Fiber - PTFE Lubricated |
|||
| Dry Time | 3 hour | 3 hour | |
| ExxonMobil Santoprene® 121-67W175 Thermoplastic Elastomer A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance, and is designed for .. |
|||
| Dry Time | 3 hour | 3 hour | |
| ExxonMobil Santoprene® 201-80 Thermoplastic Elastomer A soft, colorable, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide ra.. |
|||
| Dry Time | 3 hour | 3 hour | |
| ExxonMobil Santoprene® 251-70W232 Thermoplastic Elastomer A soft, colorable, flame retardant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material has good fluid resistance and contains non-ether brominated flame retard.. |
|||
| Dry Time | 3 hour | 3 hour | |
| ExxonMobil Santoprene® 101-55 Thermoplastic Elastomer A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range .. |
|||
| Dry Time | 3 hour | 3 hour | |
| ExxonMobil Santoprene® 241-64 Thermoplastic Elastomer A soft, colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It complies with NSF 61 for plumbing applications in contact with potable water and NSF 51 f.. |
|||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Celanese Hostaform® C 9021 TF XAP² POM, Tribological Chemical abbreviation according to ISO 1043-1: POMIt is normally not necessary to dry HOSTAFORM. However, should there be surface moisture (condensate) on the molding compound as a result of incorre.. |
|||
| Dry Time | 3 hour | 3 hour | |
| Advanced Elastomer Systems Santoprene® 251-92 Thermoplastic Rubber
(discontinued **) A colorable thermoplastic flame retardant elastomer with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloroprene, and chlorosulfonated polyethylene. It can b.. |
|||